Hierarchically macro/mesoporous silica monoliths constructed with interconnecting micrometer-sized unit rods

Under typical dilute reactant compositions (3 ~ 5 wt% of surfactant template concentration) and conventional hydrothermal conditions for mesoporous materials synthesis, successful preparation of hierarchically macro/mesoporous silica monoliths was reported in this paper. The resultant materials were characterized by a series of techniques including powder X-ray diffraction, N₂ adsorption–desorption, SEM, TEM/EDS, and Hg porosimetry. A new kind of stable and hierarchically porous pure silica monoliths was confirmed, which are featured with highly ordered mesoporous structures, rod-shaped unit particles, large specific surface area of 492 m²/g, continuous macropores of about 4.0 μm in size and high macropore volume of about 13.1 cm³/g. Moreover, using the resultant silica monoliths as hard templates, carbon monoliths have been successfully replicated, which inherit the structural characters of parent silica materials.