The effect of manganese on the microstructure and mechanical properties of zinc–aluminium based ZA-8 alloy

In this investigation, the effect of manganese as an alloying element in the range 0.01%–0.53 wt.%, on the hardness, 0.2% yield, tensile and impact strength, and creep properties of a gravity cast Zn–Al based ZA-8 alloy has been investigated. It was found that addition of Mn over the entire range of concentrations has a useful effect on the hardness of the alloy. Also, the 0.2% yield and ultimate tensile strength (UTS) of the samples did not change significantly with Mn additions up to 0.045 wt.% but decreased with a further increase in Mn content. Furthermore, the impact strength of the alloy improved with increasing Mn up to 0.045 wt.% and then decreased gradually with a further increase in Mn content. On the other hand, the creep resistance of the alloy increased continuously with increasing Mn content up to 0.53 wt.% Mn. Metallographic studies showed that addition of Mn resulted in microstructural modifications of the alloy involving the formation of complex intermetallic compound identified as MnAl₆. The increase in creep resistance and decrease in tensile and impact strength were thought to have been caused by the changing morphology and amount of the intermetallic.