Analysis of microstructure and microhardness of Zr-2.5Nb processed by High-Pressure Torsion (HPT)

Nanostructured materials have been widely studied due to the improvement of their mechanical properties comparing to those of coarse grain materials. The present work intended to analyze the microstructure and microhardness of Zr-2.5Nb processed by high-pressure torsion (HPT), one of the severe plastic deformation techniques. The deformations were carried out at room temperature using a pressure of 5 GPa and 5 anvil turns. Vickers indentation was used to evaluate the microhardness of the samples. Transmission electron microscopy and X-ray diffraction were used to analyze the microstructure. The results showed a significant refinement from the initial microstructure achieving nanometric grain size around 50 nm and phase transformation α → ω + β_I induced by shear. The Vickers microhardness values of the material submitted to HPT technique were significantly higher than those of non-deformed material. Also, HPT procedure resulted in a huge grain refinement of the material and in phase transformation.