Bi_1.5ZnNb_1.5O₇ cubic pyrochlore ceramics prepared by aqueous solution–gel method

Bi_1.5ZnNb_1.5O₇ cubic pyrochlore ceramic was successfully prepared by the aqueous solution method. The preparation, microstructure development and dielectric properties of ceramics were investigated. Homogeneous precalcined ceramics powders have a cubic pyrochlore phase after thermal treatment at the temperature as low as 450 °C. The aqueous solution–gel method, which Bi, Zn and Nb ions are chelated to form metal complexes, leading to the formation of cubic pyrochlore phase at low firing temperatures. No detectable intermediary phase such as BiNbO₄ or pseudo-orthorhombic pyrochlore is observed in the XRD patterns of ceramics at the sintering temperature range from 850 to 1,000 °C. The dielectric properties study revealed that the ceramics sintered at 900 °C show excellent performance with dielectric constant of 111 and dielectric loss of 2.3871 × 10⁻⁴ under 1 MHz at room temperature.