Production of Carbon Nanotube by Ethylene Decomposition over Silica-Coated Metal Catalysts

Formation of carbon nanofibers (CNFs) and carbon nanotubes (CNTs) through the decomposition of ethylene at 973 K was achieved using various metal catalysts covered with silica layers. CNFs of various diameters were formed by ethylene decomposition over a Co metal catalyst supported on the outer surface of the silica. In contrast, silica-coated Co catalysts formed CNTs with uniform diameters by ethylene decomposition. Silica-coated Ni/SiO₂ and Pt/carbon black also formed CNTs with uniform diameters, while CNFs and CNTs with various diameters were formed over Ni/SiO₂ and Pt/carbon black without a silica coating. These results indicate that silica layers that envelop metal particles prevent sintering of the metal particles during ethylene decomposition. This results in the preferential formation of CNTs with a uniform diameter.