Solidification Structure Refinement of 2205 Duplex Stainless Steel by Pulse Magneto-Oscillation
verfasst von : Jie Ni, Congsen Wu, Honggang Zhong, Qijie Zhai
Erschienen in: TMS 2015 144th Annual Meeting & Exhibition
Verlag: Springer International Publishing
Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
The influence of pulse magneto-oscillation (PMO) on the solidification structure of 2205 duplex stainless steel (DSS) was investigated. The influences of different treating power on solidification structure were studied by changing the peak current value. The results indicated that PMO treatment can significantly refine the equiaxed grains of 2205 DSS. The as-cast structure without PMO treatment was coarse equiaxed grains. With the increase of the treating power, the grains of 2205 DSS changed into fine equiaxed grains. The grain density increased from 3.5 grains/cm2 to 42 grains/cm2, i.e. the mean diameter of equiaxed grains decreased from 7.1 mm to 1.8 mm. Meanwhile, the grain refinement due to PMO treatment had little effect on ferrite/austenite ratio during the solidification process.