Study of defect states in a-Se₈₅Te_15−xPb_x thin films by space charge limited conduction mechanism

Current–Voltage (I–V) characteristics have been studied at various temperatures in vacuum evaporated thin films of a-Se₈₅Te_15−xPb_x (x = 0, 2, 4, 6) alloys. These characteristics show that, at low electric fields, an ohmic behaviour is observed. However, at high electric fields (E ∼ 10⁴ V/cm), the current becomes superohmic. At high fields, in case of samples having 0 and 2 at% of Pb, the experimental data fits well with the theory of space charge limited conduction (SCLC) in case of uniform distribution of localized states in the mobility gap. Such type of behaviour is not observed at higher concentration of Pb in the present glassy system due to high conductivity. In these samples, joule heating due to large currents may prohibit the measurement of SCLC. Using the theory of SCLC for the uniform distribution of the traps, the density of localized defect states near Fermi level is calculated for these compositions. The results indicate that the density of defect states near Fermi level increases on addition of Pb to binary Se₈₅Te₁₅alloy. This is explained in terms of electronegativity of Pb as compared to host elements.