Synthesis and characterization of bulk amorphous/amorphous composite alloys through powder metallurgy route
Erschienen in: Journal of Materials Science | Ausgabe 9/2008
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
In the present study, amorphous Ni60Nb20Zr20 and Ti50Cu28Ni15Sn7 alloy powders were synthesized separately using a mechanical alloying (MA) technique. The dual-amorphous-phased (Ti50Cu28Ni15Sn7)100−x(Ni60Nb20Zr20)x (x = 0, 10, 20, and 30 vol%) powders were prepared by mixing the corresponding amorphous powders. The dual-amorphous-phased powders were then consolidated into bulk amorphous/amorphous composite (BA/AC) alloy discs. The amorphization status of as-prepared powders and bulk BA/AC composite discs was confirmed by X-ray diffraction (XRD) and transmission electron microscopy (TEM). The microstructure of the BA/AC discs showed that the Ni60Nb20Zr20 phase is distributed homogeneously within the Ti50Cu28Ni15Sn7 matrix. The (Ti50Cu28Ni15Sn7)70(Ni60Nb20Zr20)30 BA/AC disc exhibited a relative density of 96.6% and its Vickers microhardness was 726 kg/mm2.