Synthesis and characterization of FePt nanoparticles and FePt nanoparticle/SiO₂-matrix composite films

Superparamagnetic face-centered cubic (fcc) FePt nanoparticles were synthesized using a polyol process. The effect of reaction temperature and molar ratio of Fe(CO)₅ to Pt(acac)₂ on the structure, composition and morphology of nanoparticles has been investigated. The optimum processing condition has been obtained for producing well-monodisperse fcc-phase FePt nanoparticles with the 2:1 molar ratio of Fe-Pt at 220 °C. In order to circumvent the problem of FePt particle coalescence during high temperature annealing for the L1₀ ordering, FePt nanoparticle/SiO₂-matrix composite films have been fabricated by sol–gel method. The experimental results confirm that the amorphous SiO₂ matrix effectively inhibits the grain growth and particle aggregation during 700 °C annealing for 1 h. Well-monodisperse face-centered tetragonal (fct) FePt particles embedded in the SiO₂ matrix can be obtained with the long-range chemical order parameter S of ~0.74, indicating partially ordered L1₀ phase transition in FePt/SiO₂ composite films. The FePt/SiO₂ system exhibits a hysteretic behavior with smaller coercive field of 1,450 Oe. The incomplete phase transition from cubic deredat height maxsium (A ₁-disordered phase to tetragonal L1₀-ordered phase) might be responsible for it.