The influence of CdSe and ZnSe nanoparticles on the optical properties of Sm³⁺ ions in lead borate glasses

The effect of glass composition and the presence of CdSe/ZnSe nanoparticles (NPs) on the optical absorption and fluorescence of Sm-doped lead borate glasses are studied. Three sets of glass samples xPbO:(99.5-x) B₂O₃:0.5Sm₂O₃, x = 29.5–69.5 mol%, xPbO:(96.5-x) B₂O₃:0.5Sm₂O₃: 3CdSe/ZnSe, x = 36.5, and 56.5 mol% are prepared. NPs are grown by annealing these glasses just below the glass transition temperature. Average size of both types of NPs increases with annealing time; however, CdSe NPs grew to a larger size range (2 to 20 nm) compared to ZnSe NPs (1 to 16 nm). We analyzed the hypersensitive transition, intensity parameters, radiative transition probability, stimulated emission cross section (σ_p), and the area ratio of the electric dipole/magnetic dipole transitions of Sm³⁺. The intensity parameters show a minimum at 11 h annealing for 36.5 mol% and a maximum for the same annealing duration in 56.5 mol% PbO containing CdSe NPs. The σ_p for 56.5 mol% of PbO with CdSe NPs is found to be a maximum when the average NP size is around 14 nm. ZnSe NPs containing glasses also show significant changes in σ_p when the average particle size is ~16 nm, for 36.5 mol% PbO. Our results suggest that the optical properties of Sm³⁺ in lead borate glasses are sensitive to its electronic environment which can be modified by varying the base glass composition and/or incorporating large NPs of CdSe/ZnSe. The large σ_p values that we observe for some of the glass compositions make them attractive materials for photonic devices and photovoltaic applications.