The Relationship between Dendrite Arm Spacing and Cooling Rate of Al-Si Casting Alloys in High Pressure Die Casting
verfasst von : Jae-Ik Cho, Cheol-Woo Kim, Young-Chan Kim, Se-Weon Choi, Chang-Seog Kang
Erschienen in: ICAA13 Pittsburgh
Verlag: Springer International Publishing
Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
The effects of cooling rate on the solidification behavior of Al-8.5%Si-3%Cu and Al-11%Si-3%Cu alloys were studied during high pressure die casting (HPDC). The HPDC experiment was conducted by using the dies with 3 steps for 3 different cooling rates. Because of the high in both melt temperature and pressure, it was difficult to obtain the temperature profile directly from HPDC specimen. Therefore, in this study, cylindrical bar castings with different diameter were poured to acquire the cooling curves at the solidification range of 15°C/s up to 100°C/s and then the microstructures were compared to estimate the cooling rate in HPDC. The solidification characteristics including liquidus/solidus temperature and dendrite arm spacing of each alloy and each cooling rate was analyzed and the results showed strong proportional relationship between dendrite arm spacing and cooling rate in HPDC. The results were also compared with the actual die casting specimens and MAGMA simulation.