Abstract

The failure of BOF hood tube is a common industrial problem that has received little attention in literature. The major mode of failure as observed by most of the industries is thermal fatigue failure. Earlier people have studied the thermal stress profile in hood system considering constant water temperature. However, in reality there are fluctuations in water temperature due to cyclic thermal load caused by BOF gas. Present study reveals that the water temperature fluctuation is having significant impact in causing thermal fatigue failure. The change in water velocity and tube thickness has negligible effect in thermal fatigue failure compared to that observed for water temperature fluctuation. However, tube material of construction is also having significant impact on its failure.

Vorheriger Artikel Bronze Alloy Development for Zinc Vapor Capture

Nächster Artikel Failure Analysis of AISI 440C Steel Ball Screws Used in the Actuator System of a Satellite Launch Vehicle

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Nur mit Berechtigung zugänglich

T. Ondrey, Improvements made to USS Edgar Thomson BOF hood system, in AISE Conference on Prolonging BOF Hood Life (Nashville, Tennessee, 1998)

M.L. Wei, Survey of BOF hoods in North America. Iron Steel Eng. 75(4), 25–30 (1998)

M.L. Wei, International Survey of BOF hoods, in Conference Proceedings of BOF Hoods for the 21st Century (Nashville, Tennessee, 2000)

R.E. Hargraave, D.J. Kotwica, Common failure mechanisms in BOF hoods. Iron Steel Eng. 73(11), 22–28 (1996)

I.V. Samarasekera, Mathematical modeling of thermal stresses in basic oxygen furnace hood tubes. Met. Trans. B 16(2), 247–261 (1985)CrossRef

S.K. Saha, D.J. Radakovic, T.A. Walden, Life extension of BOF lower hood at U. S. Steel Canada’s Lake Erie Works via engineering and design changes, in AISTech Proceedings (Pittsburgh, 2013), pp. 929–938

J.F. Mcgurn, Composite tubes in black liquor recovery boilers: an update. Pulp Pap. Canada 94, 12 (1993)

H.C. Hottel, Radiant Heat Transmission, 3rd edn, Chap. 4, Heat Transmission (McGraw-Hall Book Company, New York, 1964)

G.A. Stemetzki, M.M. Kuta, C. Shepard, BOF hood life cycle cost improvement program. Iron Steel Technol. 1(1), 54–67 (2004)

10.

L.C. Boyd Jr., V.K. Sikka, Aluminum bronze alloys to improve the system life of basic oxygen and electric arc furnace hoods, roofs and side vents. Final Report, U. S. Department of Energy (DOE) Information Bridge, 2006, p. 22

11.

J.T.P. Castro, R.D. Vieira, A.C.N. Vidal, A.C.O. Miranda, J.L.F. Freire, M.A. Meggiolaro, A case study on corrosion-thermal fatigue damage, R. Marquês de S. Vicente, Rio de Janeiro, Brazil, unpublished literature, 2005

12.

J.D. Zupanovich, Oxidation and Degradation Products of Common Oxygen Scavengers. Report (Chem Tech Inc., USA, 2002)

13.

P.K. Das, A.K. Gupta, N. Nirmalkar, R.P. Chhabra, Effect of confinement on forced convection from a heated sphere in Bingham plastic fluids. Korea Austrailia Rheol. J. 27(2), 75–94 (2015)CrossRef

Titel: Transient Thermal Stress Analysis of BOF Hood Failure
verfasst von: P. K. Das
S. Sarkar
S. K. Ajmani
Publikationsdatum: 01.06.2017
Verlag: Springer US
Erschienen in: Journal of Failure Analysis and Prevention / Ausgabe 3/2017
Print ISSN: 1547-7029
Elektronische ISSN: 1864-1245
DOI: https://doi.org/10.1007/s11668-017-0267-6

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht

Springer Professional

Abstract

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Technik"

Springer Professional "Wirtschaft+Technik"

Weitere Artikel der Ausgabe 3/2017

Events

Metal Dusting of Process Gas Heater Convection Tubes

Creep Life Degradation and Microstructure Degeneration in a Low-Pressure Turbine Blade of a Military Aircraft Engine

Transverse Cracking of HF-ERW Pipes

Impact of Internal Pipe Grooves on Flow-Accelerated Corrosion of Small-Bore A-106 Carbon Steel Pipes

Estimation of Fretting Wear-Limited Life of a Shell and Tube Heat Exchanger Tubes: Analytical Formulation, Computer Implementation and Qualification Against Actual Reported Failure

Premium Partner

Marktübersichten