X-ray diffraction, optical absorption and emission studies on Er³⁺- and Er³⁺/Yb³⁺-doped Li₃NbO₄ powder

Er³⁺(/Yb³⁺)-doped Li₃NbO₄ powder were prepared by thermally sintering mixtures of Er₂O₃ (0.5, 1.0 mol%), Yb₂O₃ (0, 0.5, 1.0 mol%), Li₂CO₃ (48–49 mol%) and Nb₂O₅ (50 mol%) at 1125, 1150 and 1450 °C over the durations of 8–22 h. The crystalline phases contained in these samples were determined by using X-ray diffraction and discussed in comparison with a vapor-transport-equilibration-treated (VTE-treated) Er(2.0 mol%):LiNbO₃ single crystal and ErNbO₄ powder previously reported. The results show that the X-ray patterns of the rare-earth-doped samples reveal little difference each other, but large differences with those of the VTE crystal and ErNbO₄ powder. The doped rare-earth ions Er³⁺ (and Yb³⁺) present in the powder as the ErNbO₄ (and YbNbO₄) phase(s). The possibility that the highly Er-doped LiNbO₃ crystal contains Li₃NbO₄ precipitates is small. Optical absorption and emission studies show that the only Er-doped Li₃NbO₄ powder shows similar absorption and emission characteristics with the pure ErNbO₄. The codopant Yb³⁺ ion enhances the 980-nm-upconversion emissions of Er³⁺ ions, results in remarkable spectral alterations at 0.98 μm region, and causes the alterations of relative absorbance and relative emission intensity of individual peaks or bands at 1.5 μm region. On the other hand, the Yb-codoping hardly affects the Er³⁺ energy structure and the lifetime of Er³⁺ ion at 1.5 μm. The measured lifetimes at 1.5 μm of Er³⁺ ions in the singly Er³⁺- and doubly Er³⁺/Yb³⁺-doped mixtures have a nearly same value of ∼ 1.5 ms. For the pure ErNbO₄ powder, the lifetime is prolonged to ∼2 ms perhaps due to radiation trapping effect.