Alumina Scale Adherence to CoCrAl Alloys and Coatings
verfasst von : D. P. Whittle, D. H. Boone
Erschienen in: Surfaces and Interfaces in Ceramic and Ceramic — Metal Systems
Verlag: Springer US
Enthalten in: Professional Book Archive
Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
There are two essential requirements for alloys or coatings which are designed to withstand degradation by oxidation during high temperature exposure. First, they must form a surface oxide which thickens only at a slow rate, and secondly this oxide layer must remain adherent to the alloy surface under all conditions. A12O3 is generally regarded as the best protective oxide: diffusion through A12O3 is relatively slow in comparison with most other oxides, and since it is also stable, relatively little difficulty exists in selecting a composition which contains sufficient aluminium to provide, by selective oxidation, a protective A12O3 scale under various service environments. Typically, these will contain at least 5% A1 (by mass) and usually substantial amounts of Cr.