Metallurgical and Materials Transactions A

Erschienen in:

03.01.2021 | Communication

Anomalous Tension Twinning Activity in Extruded Mg Sheet During Hard-Orientation Loading at Room Temperature

verfasst von: Y. Q. Chai, C. J. Boehlert, Y. F. Wan, G. H. Huang, H. Zhou, J. Zheng, Q. D. Wang, D. D. Yin

Erschienen in: Metallurgical and Materials Transactions A | Ausgabe 2/2021

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

The surface twins were characterized for a strongly basal-textured Mg sheet that was deformed under tension in the extrusion direction (hard-orientation). All the twins observed were tension twins. A significant number of them exhibited negative Schmid factor (m) and Luster–Morris parameter (m′) values. Both a normalized m and grain-boundary misorientation were correlated to the twinning behavior, which was shown to be more dependent on the local conditions than the globally applied stress, thereby limiting the m and m′ correlations.

Graphic Abstract

Vorheriger Artikel Machine Learning Approach to Design High Entropy Alloys with Heterogeneous Grain Structures

Nächster Artikel Novel Approach of Electroshock Treatment for Defect Repair in Near-β Titanium Alloy Manufactured via Directed Energy Deposition

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Nur mit Berechtigung zugänglich

[1] M. A. Kumar and I. J. Beyerlein: J. Mater. Res., 2020, vol. 35, pp. 217-241.CrossRef

[2] M. H. Yoo and J. K. Lee: Philos. Mag. A, 1991, vol. 63, pp. 987-1000.CrossRef

[3] L. Capolungo, P. E. Marshall, R. J. Mccabe, I. J. Beyerlein and C. N. Tomé: Acta Mater., 2009, vol. 57, pp. 6047-6056.CrossRef

[4] I. J. Beyerlein, L. Capolungo, P. E. Marshall, R. J. Mccabe and C. N. Tomé: Philos. Mag., 2010, vol. 90, pp. 2161-2190.CrossRef

[5] C. D. Barrett, H. El Kadiri and M. A. Tschopp: J. Mech. Phys. Solids, 2012, vol. 60, pp. 2084-2099.CrossRef

J. Čapek, K. Máthis, B. Clausen and M. Barnett: Acta Mater., 2017, vol. 130, pp. 319-328.CrossRef

[7] M. A. Kumar, I. J. Beyerlein and C. N. Tomé: Acta Mater., 2016, vol. 116, pp. 143-154.CrossRef

[8] I. J. Beyerlein, R. J. Mccabe and C. N. Tomé: J. Mech. Phys. Solids, 2011, vol. 59, pp. 988-1003.CrossRef

[9] M. A. Kumar, B. Clausen, L. Capolungo, R. J. Mccabe, W. Liu, J. Z. Tischler and C. N. Tomé: Nat. Commun., 2018, vol. 9, pp. 1-8.CrossRef

10.

[10] F. Wang, S. Sandlöbes, M. Diehl, L. Sharma, F. Roters and D. Raabe: Acta Mater., 2014, vol. 80, pp. 77-93.CrossRef

11.

[11] J. Koike, Y. Sato and D. Ando: Mater. Trans., 2008, vol. 49, pp. 2792-2800.CrossRef

12.

[12] S. H. Park, S. Hong and C. S. Lee: Scripta Mater., 2010, vol. 62, pp. 202-205.CrossRef

13.

[13] S. Mu, J. J. Jonas and G. Gottstein: Acta Mater., 2012, vol. 60, pp. 2043-2053.CrossRef

14.

[14] R. Xin, Y. Liang, C. Ding, C. Guo, B. Wang and Q. Liu: Mater. Des., 2015, vol. 86, pp. 656-663.CrossRef

15.

[15] C. J. Boehlert, Z. Chen, I. Gutiérrez-Urrutia, J. Llorca and M. T. Pérez-Prado: Acta Mater., 2012, vol. 60, pp. 1889-1904.CrossRef

16.

[16] É. Martin, L. Capolungo, L. Jiang and J. J. Jonas: Acta Mater., 2010, vol. 58, pp. 3970-3983.CrossRef

17.

[17] J. J. Jonas, S. Mu, T. Al-Samman, G. Gottstein, L. Jiang and Ė. Martin: Acta Mater., 2011, vol. 59, pp. 2046-2056.CrossRef

18.

[18] M. A. Kumar, M. Wroński, R. J. Mccabe, L. Capolungo, K. Wierzbanowski and C. N. Tomé: Acta Mater., 2018, vol. 148, pp. 123-132.CrossRef

19.

[19] M. D. Nave and M. R. Barnett: Scripta Mater., 2004, vol. 51, pp. 881-885.CrossRef

20.

[20] J. Luster and M. A. Morris: Metall. Mater. Trans. A, 1995, vol. 26, pp. 1745-1756.CrossRef

21.

[21] T. R. Bieler, R. Alizadeh, M. Peña-Ortega and J. Llorca: Int. J. Plasticity, 2019, vol. 118, pp. 269-290.CrossRef

22.

[22] T. R. Bieler, P. Eisenlohr, C. Zhang, H. J. Phukan and M. A. Crimp: Curr. Opin. Solid State Mater. Sci., 2014, vol. 18, pp. 212-226.CrossRef

23.

[23] S. Haouala, R. Alizadeh, T. R. Bieler, J. Segurado and J. Llorca: Int. J. Plasticity, 2020, vol. 126, pp. 102600.CrossRef

24.

[24] R. Hielscher, C. Silbermann, E. Schmidl and J. Ihlemann: J. Appl. Crystallogr., 2019, vol. 52, pp. 984-996.CrossRef

25.

[25] F. Bachmann, R. Hielscher and H. Schaeben: Solid State Phenom., 2010, vol. 160, pp. 63-68.CrossRef

26.

[26] L. J. Long, G. H. Huang, D. D. Yin, B. Ji, H. Zhou and Q. D. Wang: Metall. Mater. Trans. A, 2020, vol. 51, pp. 2738-2751.CrossRef

27.

[27] G. H. Huang, D. D. Yin, J. W. Lu, H. Zhou, Y. Zeng, G. F. Quan and Q. D. Wang: Mater. Sci. Eng. A, 2018, vol. 720, pp. 24-35.CrossRef

28.

[28] J. W. Lu, D. D. Yin, G. H. Huang, G. F. Quan, Y. Zeng, H. Zhou and Q. D. Wang: Mater. Sci. Eng. A, 2017, vol. 700, pp. 598-608.CrossRef

29.

[29] H. Fan, S. Aubry, A. Arsenlis and J. A. El-Awady: Scripta Mater., 2016, vol. 112, pp. 50-53.CrossRef

30.

[30] C. M. Cepeda-Jiménez, J. M. Molina-Aldareguia and M. T. Pérez-Prado: Acta Mater., 2015, vol. 88, pp. 232-244.CrossRef

31.

[31] P. E. Marshall, G. Proust, J. T. Rogers and R. J. Mccabe: J. Microsc., 2010, vol. 238, pp. 218-229.CrossRef

32.

[32] O. Muránsky, L. Balogh, M. Tran, C. J. Hamelin, J. S. Park and M. R. Daymond: Acta Mater., 2019, vol. 175, pp. 297-313.CrossRef

33.

LS Toth, CF Gu, B Beausir, JJ Fundenberger, M Hoffman: Acta Mater., 2016, vol. 117, pp. 35-42CrossRef

34.

[34] A. Githens, S. Ganesan, Z. Chen, J. Allison, V. Sundararaghavan and S. Daly: Acta Mater., 2020, vol. 186, pp. 77-94.CrossRef

35.

[35] W. Z. Abuzaid, M. D. Sangid, J. D. Carroll, H. Sehitoglu and J. Lambros: J. Mech. Phys. Solids, 2012, vol. 60, pp. 1201-1220.CrossRef

36.

[36] Z. Z. Shi, Y. Zhang, F. Wagner, P. A. Juan, S. Berbenni, L. Capolungo, J. S. Lecomte and T. Richeton: Acta Mater., 2015, vol. 83, pp. 17-28.CrossRef

37.

[37] K. D. Molodov, T. Al-Samman, D. A. Molodov and G. Gottstein: Acta Mater., 2016, vol. 103, pp. 711-723.CrossRef

38.

[38] W. Pantleon: Scripta Mater., 2008, vol. 58, pp. 994-997.CrossRef

39.

[39] D. D. Yin, Q. D. Wang, C. J. Boehlert, Z. Chen, H. M. Li, R. K. Mishra and A. Chakkedath: Metall. Mater. Trans. A, 2016, vol. 47, pp. 6438-6452.CrossRef

40.

[40] H. Wang, C. J. Boehlert, Q. D. Wang, D. D. Yin and W. J. Ding: Int. J. Plasticity, 2016, vol. 84, pp. 255-276.CrossRef

41.

[41] M. A. Kumar, I. J. Beyerlein, R. J. Mccabe and C. N. Tomé: Nat. Commun., 2016, vol. 7, pp. 1-9.

Titel: Anomalous Tension Twinning Activity in Extruded Mg Sheet During Hard-Orientation Loading at Room Temperature
verfasst von: Y. Q. Chai
C. J. Boehlert
Y. F. Wan
G. H. Huang
H. Zhou
J. Zheng
Q. D. Wang
D. D. Yin
Publikationsdatum: 03.01.2021
Verlag: Springer US
Erschienen in: Metallurgical and Materials Transactions A / Ausgabe 2/2021
Print ISSN: 1073-5623
Elektronische ISSN: 1543-1940
DOI: https://doi.org/10.1007/s11661-020-06093-5

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht

Springer Professional

Abstract

Graphic Abstract

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Springer Professional "Technik"

Weitere Artikel der Ausgabe 2/2021

Hydrogen Desorption Behavior Trapped in Various Microstructures of High-Strength Steels Using Thermal Desorption Analysis

Fracture Resistance of Advanced High-Strength Steel Sheets for Automotive Applications

In Situ Study on Interrupted Growth Behavior and Crystallography of Bainite

Enhancing Surface Hardness of Titanium Through Ni-Ti Intermetallic Microstructures Formed In Situ During Weld Deposition of Nickel

Effects of Native AlN Particles on Heterogeneous Nucleation in an Al-3Fe Alloy

Relationship Among Tensile Strength, High Cycle Fatigue Strength, and Origin of Fatigue Crack Initiation in a Minor Boron (B)-Modified β-Type Ti-6.8Mo-4.5Fe-1.5Al Alloy

Premium Partner

Marktübersichten