Comparative analysis of thermally modified and native spruce loaded perpendicular to the grain
Erschienen in: European Journal of Wood and Wood Products | Ausgabe 3/2010
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
The aim of this work was to analyse the material behaviour of thermally modified and native spruce by load applied perpendicularly to the grain. Therefore, thermally modified and native samples were prepared for bending tests with the load in tangential direction. The bending strength in radial direction decreases significantly with the thermal treatment. The fracture surfaces in the tangential section of the bending samples after testing were analysed with a scanning electron microscope. For native samples, the typical failure was found in the intercellular area. For thermally modified samples, failure of the entire cell wall was observed. The material behaviour is more brittle, as demonstrated by the load-deflection curves, but also by anatomical studies of the fracture surfaces.