Comparison between the effects of CdCl2 heat treatment on CdTe films prepared by RF magnetron sputtering and close spaced sublimation methods
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 7/2013
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
CdTe films were prepared on Fluorine-doped tin oxide substrate by RF magnetron sputtering and close spaced sublimation (CSS) methods, respectively. These CdTe films were then treated with a wet CdCl2 heat process at different temperatures. The structural and optical properties of CdTe films were investigated by X-ray diffraction, scanning electron microscope and UV–Visible spectrophotometer. The results reveal that both types of CdTe films have a better crystalline and larger grain size after CdCl2 heat treatment. However, the (422) peak has a more preferential orientation than (511) peak after CdCl2 activation for CdTe films prepared by sputtering method, while these two peaks almost have the same intensity for CSS-prepared CdTe films. The transmittance of CdTe films prepared by CSS is apparently lower than sputtered CdTe films. Correspondingly, the efficiency of solar cells with CSS-prepared CdTe is 7.3, 2.6 % of sputtered CdTe films.