Compositional effects on the properties of (1-x)BaTiO₃-xBi_0.5Na_0.5TiO₃ ceramics

The compositional effects on the crystal structure, phase transition, dielectric, ferroelectric and piezoelectric properties of the (1-x)BaTiO₃-x(Bi_0.5Na_0.5)TiO₃ solid solution ceramics were investigated. After sintering at 1200 °C for 2 h, the ceramics with different content of (Bi_0.5Na_0.5)TiO₃ (BNT) formed single-phase solid solutions with perovskite structure. The lattice constant c/a ratio of the solid solutions decreased as BNT content increased except that with 20 mol% BNT, which had the largest value of c/a ratio for all samples. The second phase transition corresponding to BaTiO₃ (BT) at about 5 °C shifted to low temperature and gradually disappeared as BNT increased. A new secondary phase transition appeared at 32 °C and 64 °C, respectively, when BNT content was 5 and 14 mol%. The Curie temperature, T _c, shifted in the temperature range between 112 °C and 166 °C, and the remanent polarization, P _r, decreased whereas the coercive field, E _c, increased as the BNT content increased. The relatively high value of piezoelectric coefficient d₃₃ together with a relatively high Curie temperature and low loss tangent and stable dielectric properties were obtained when the addition of BNT was 20 mol%.