Effect of Porosity on Deformation, Damage, and Fracture of Cast Steel

A combined experimental and computational study is performed to investigate the effect of centerline shrinkage porosity on deformation, damage, and fracture of cast steel under tensile testing. Steel plates containing shrinkage porosity are cast in sand molds, machined into test coupons, and tensile tested to fracture. The average volumetric porosity in the gage section of the specimens with porosity ranges from 0.10 to 0.27 pct. Ductility in the test castings with porosity is markedly reduced with the percent elongation data ranging from 12.8 to 19.6 pct; vs 22 pct elongation for the sound material. Radiographic imaging is used to measure and reconstruct the porosity field in the test specimens. The reconstructed porosity field is then used in a finite-element stress analysis simulating the tensile testing. Local elastic properties are reduced according to the porosity fraction present. Porous metal plasticity theory is used to model the damage due to porosity and the fracture. Good agreement is obtained between the measured and predicted stress–strain curves and fracture behaviors. The reduction in ductility is predicted well by comparing the measured and the simulated elongations. The computational modeling approach used in this study allows for a detailed evaluation of the effect of porosity, including its size, shape, and location, on the fracture behavior of steel castings.