Effects of Nb₂O₅ doping on the microstructure and the dielectric temperature characteristics of barium titanate ceramics

In this work, the effects of Nb₂O₅ addition on the dielectric properties and phase formation of BaTiO₃ were investigated. A core–shell structure was formed for Nb-doped BaTiO₃ resulted from a low diffusivity of Nb⁵⁺ ions into BaTiO₃ when grain growth was inhibited. In the case of 0.3–4.8 mol% Nb₂O₅ additions, two dielectric constant peaks were observed. The Curie dielectric peak was determined by the ferroelectric-paraelectric transition of grain core, whereas the secondary broad peak at lower temperature was due to strong chemical inhomogeneity in Nb-doped BaTiO₃ ceramics. The dielectric constant peak at Curie temperature was markedly depressed with the addition of Nb₂O₅. On the other hand, the secondary dielectric constant peak was enhanced when sintered above 1280 °C for higher Nb₂O₅ concentrations (≥1.2 mol%). The Curie temperature was shifted to higher temperatures, whereas the transition temperature corresponding to the secondary peak moved to lower temperatures as increasing the amount of Nb₂O₅ more than 1.2 mol%. The decrease of this lower transition temperature was assumed to be closely related with the secondary phase formation when Nb concentration greater than 1.2 mol%. From XRD analyses, a large amount of secondary phases was observed when Nb₂O₅ amount exceeded 1.2 mol%. The coefficients of thermal expansion of Nb-doped BaTiO₃ were increased with increasing Nb₂O₅ contents, resulting in large internal stress between cores and shells. Therefore, the shift of Curie temperature to higher temperatures was attributed to internal stress resulting from the formation of a core–shell structure and a large amount of secondary phase grains.