16. Fatigue in Welds

verfasst von : Pietro Paolo Milella

Erschienen in: Fatigue and Corrosion in Metals

Verlag: Springer International Publishing

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

More than half a century is passed from World War II when welding heavily entered into engineering practice and in the naval construction technique, in particular, often with catastrophic results. As in the development of any technological field it took its toll of failures and casualties before welding would become a discipline of its own and institutes, research centers, universities and industries would develop enough knowledge to provide good practices and standards.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Vorheriges Kapitel Crack Tip Plastic Zone Effect on Fatigue Crack Propagation

Nächstes Kapitel Corrosion

Solidification and Phase Transformations in Welding. Suranaree University of Technology, Thailand (2007)

La Vecchia, G.M.: Il Giunto Saldato: Microstruttura e Principali Difetti (in Italian). University of Brescia, Department of Mechanical Engineering, Bresia, Italy

Masubuchi, K.: Control of Distortion and Shrinkage in Welding. In: Welding Research Council Bulletin No. 149 (April 1970)

UKAEA: An Assessment of the Integrity of PWR Pressure Vessels. 2nd Report by Dr. W. Marshall Study Group (March 1982)

Kanazawa, T., Oba, H., Susei, S.: The effect of welding residual stress upon brittle fracture propagation, Report II. Jpn Soc. Naval Arch. 110, 359–368 (1961)

Masubuchi, K., Martin, D.C.: Investigation of Residual Stresses in Steel Weldments. Battelle Memorial Inst., Columbus, Ohio, Defense Technical Information Center (1998)

Kihara, H., Masubuchi, K., Kusuda, T., Iida, K.: IIW-X-219 (1959)

Nichols, R.W.: The use of overstressing technique to reduce the risk of subsequent brittle fracture. In: A Review Prepared for Commission X, vol. IIW, pp. X-409–67E (1967)

Liljeblad, R.: ASEA J. 23 (1937)

10.

Kihara, H., Masubuchi, T., Iida, K., Oba, H.: Report to the IIW Commission vol. X, p. X-218 (1959)

11.

Harrison, T.C., Farnehough, G.D.: The influence of warm prestressing on the brittle fracture of structures containing sharp defects. Trans. Am. Soc. Mech. Eng. 94(Series D), 373–386 (1972)

12.

Loss, F.J., Gray, R.A. Jr., Hawtorne, J.R.: Significance of Warm Prestressing to Crack Initiation During Thermal Shock. Naval Research Laboratory (September, 1977)

13.

Loss, F.J., Gray, R.A. Jr., Hawtorne, J.R.: Investigation of Warm Prestressing for the Case of Small ΔT During a reactor LOCA. Naval Research Laboratory (March, 1978)

14.

McGowan, J.J.: An Assessment of the Beneficial Effects of Warm Prestressing on the Fracture Properties of Nuclear Reactor Vessels Under Severe Thermal Shock. Westinghouse Nuclear Energy Systems, WCAP-9178 (March, 1978)

15.

Stonesifer, R.B., Rybicki, E.F., McCabe, D.E.: Warm Prestress Modeling: Comparison of Models and Experimental Results. Material Engineering Associates, Inc., NUREG/CR-5208, MEA-2305 (1989)

16.

Loss, F.J.: Structural Integrity of Water reactor Pressure Boundary Components. Naval Research Laboratory, NRL/NUREG-3512 (May, 1977)

17.

Maddox, S.J.: An Introduction to Fatigue of Welded Joints, Improving the Fatigue Strength of Welded Joints. TWI (1983)

18.

Maddox, S.J.: Fatigue assessment of weld structures. IIW Weld. World 32, 33–42 (1993)

19.

Code of Practice of Fatigue Design and Assessment of Steel Structures, BS 7608: 1993. British Standard Institution, London (1993)

20.

Gurney, T.R.: Fatigue of Welded Structures, 2nd edn. Cambridge University Press, UK (1979)

21.

Maddox, S.J.: Fatigue Strength of Welded Structures, 2nd edn. Abington Publishing, Cambridge (1991)

22.

Niu, X., Glinka, G.: The weld profile effect on stress intensity factor in weldments. Int. J. Fract.Fract. 35, 3–20 (1987)CrossRef

23.

Gordon, J.R.: Improving the fatigue life of welded structures. In: Fatigue Improvement Seminar. American Bureau of Shipping (April, 1993)

24.

Shimokawa, H., Takena, K., Itoh, F., Miki, K.: Fatigue strength of large gasset joints of 800 MPa class steel. JSCE 1 (1985)

25.

Haangsen, P.J.: Improving the strength of welded joints. In: Almar-Naess, A. (ed.) Fatigue Handbook. Tapir, Trondheim (1985)

26.

Kado, S., et al.: Influence of the Conditions in TIG Dressing on the Fatigue strength in Welded High Tensile Strength Steels. IIW Document XIII-771-75 (1975)

27.

Ambriz, R.R., Mesmacque, G., Benhamena, A., Ruiz, A., Amrouche, A., López, V.H.: Fatigue Crack Growth Behavior oin 6061-T6 Aluminum Alloy Welds Obtained by MIEA (2010)

28.

Clarck, W.G., Ir.: Fatigue Crack Growth Characteristics of ASTM A 533 Grade B, Class 1 Steel Base Plate, Weld Metal and Heat-Affected-Zone. Westinghouse Research Report 69-7E7-BFPWR-R2 (1969)

29.

Parry, M., Nordberg, H., Herzberg, R.W.: Fatigue Crack Propagation in A514 Base Plate and Welded Joints

Titel: Fatigue in Welds
verfasst von: Pietro Paolo Milella
Verlag: Springer International Publishing
Buch: Fatigue and Corrosion in Metals
Print ISBN: 978-3-031-51349-7

Electronic ISBN: 978-3-031-51350-3

Copyright-Jahr: 2024
DOI: https://doi.org/10.1007/978-3-031-51350-3_16

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht