01.01.2012 | Originals Originalarbeiten

Fire-retardant properties of wood particleboards treated with boric acid

verfasst von: Roger Pedieu, Ahmed Koubaa, Bernard Riedl, Xia-Ming Wang, James Deng

Erschienen in: European Journal of Wood and Wood Products | Ausgabe 1-3/2012

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

The fire-retardant performance of wood particleboards treated with three percentages (8, 12, and 16%) of boric acid was determined. Particles were treated during wood particles blending with adhesive. Fire-retardant properties were measured according to ASTM D3806 Standard Test Method of Small-Scale Evaluation of Fire-Retardant Paints, (2-Foot Tunnel Method). Particleboards treated with 16% boric acid showed the best fire-retardant properties, particularly in terms of weight loss, flame spread speed and afterflame time. The use of white birch inner bark particles as dispersant also lowered particleboard weight loss during fire testing. The use of boric acid not only decreased the flame spread speed but also greatly improved the internal bond and thickness swelling of manufactured particleboards over controls.

Vorheriger Artikel Oil uptake by wood during heat-treatment and post-treatment cooling, and effects on wood dimensional stability

Nächster Artikel Critical heat flux densities of various flooring materials for outdoor applications

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 340 Zeitschriften

aus folgenden Fachgebieten:

Bauwesen + Immobilien
Business IT + Informatik
Finance + Banking
Management + Führung
Marketing + Vertrieb
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

ASTM D 1037-99 (2005) Standard test methods for evaluating properties of wood-based fiber and particle panel materials. In: ASTM annual book of standards, vol 04.10. West Conshohocken, PA, pp 140–170

ASTM D 3806-98 (2001) Standard test method of small-scale evaluation of fire-retardant paints (2-foot tunnel method). In: ASTM annual book of standards, vol 06.01. West Conshohocken, PA, pp 420–424

Ayrilmis N, Candan Z, White R (2007) Physical mechanical and fire properties of oriented strandboard with fire retardant treated veneers. Holz Roh- Werkst 65:449–458 CrossRef

Basson GR, Conradie WE (2001) Preservative and fire-retardant composition and combination and process. United States Patent # 6319431

Hshieh FY, Beeson HD (1997) Flammability testing of flame-retarded epoxy composites and phenolic composites. Fire Mater 21:41–49 CrossRef

Hume J (1992) Assessing the fire performance characteristics of GRP composites. In: International conference on materials and design against fire, London, pp 11–15

Luneva NK, Petrovskaya LI (2008) Performance of intumescent fire retardant for wood. Russ J Appl Chem 81(4):704–707. ISSN 1070-4272 CrossRef

Montgomery DC (1997) Design and analysis of experiments, 4th edn. Arizona State University

Mouritz AP, Gibson AG (2006) Fire properties of polymer composite material. Springer, Berlin, pp 59–101, Chap 3

Pereyra AM, Giudice CA (2009) Flame-retardant impregnants for woods based on alkaline silicates. Fire Saf J 44:497–503 CrossRef

Plotnikova GV, Egorov AN, Khaliullin AK (2003) Flame retardants for wood, based on urea-formaldehyde resin with mineral filler. Russ J Appl Chem 76(2):310–313 CrossRef

Rowell RM, LeVan-Green SL (2005) Thermal properties. In: Rowell RM (ed) Handbook of wood chemistry and wood composites, Boca Raton, London, New York, Washington, DC, pp 121–138, Chap 6

Saka S, Sasaki M, Tanahashi M (1992) Wood-inorganic composites prepared by sol-gel processing. I. Wood-inorganic with porous structure. Mokuzai Gakkaishi 38(11):1043–1049

Tang Y, Wang DY, Jing XK, Ge XG, Yang B, Wang YZ (2008) A formaldehyde-free flame retardant wood particleboard system based on two-component polyurethane adhesive. J Appl Polym Sci 108:1216–1222 CrossRef

Terzi E, Kartal SN, White RN, Shinoda K, Imamura Y (2009) Fire performance and decay resistance of solid wood and plywood treated with quaternary ammonia compounds and common fire retardants. Eur J Wood Prod

Yunchu H, Peijang Z, Songheng Q (2000) TG-DTA studies on wood treated with flame-retardants. Holz Roh- Werkst 58:35–38 CrossRef

Titel: Fire-retardant properties of wood particleboards treated with boric acid
verfasst von: Roger Pedieu
Ahmed Koubaa
Bernard Riedl
Xia-Ming Wang
James Deng
Publikationsdatum: 01.01.2012
Verlag: Springer-Verlag
Erschienen in: European Journal of Wood and Wood Products / Ausgabe 1-3/2012
Print ISSN: 0018-3768
Elektronische ISSN: 1436-736X
DOI: https://doi.org/10.1007/s00107-011-0538-y

Springer Professional

Abstract

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Springer Professional "Wirtschaft"

Springer Professional "Technik"

Weitere Artikel der Ausgabe 1-3/2012

Effects of post-layup ammoniacal copper zinc arsenate treatment on appearance and flexural properties of Douglas-fir glued laminated beams

Einfluss der thermischen Modifizierung von Holz auf das Wasserrückhaltevermögen (WRV-Wert)

Rapid determination of formaldehyde emission potentials of binders for the woodworking industry

Ammonia vs. thermally modified timber—comparison of physical and mechanical properties

Critical heat flux densities of various flooring materials for outdoor applications

Effect of pre-pressing of veneer on the glueability and properties of veneer-based products