In situ 3-hexylthiophene polymerization onto surface of TiO2 based hybrid solar cells
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 7/2010
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
A novel configuration of hybrid solar cells fabricated using TiO2 and in situ polymerization of poly(3-hexylthiophene), or P3HT, on the surface of TiO2 is reported. Comparison of UV–Vis absorption and current/voltage (I/V) characteristics of devices with or without in situ polymerized P3HT layer were discussed, and the surface morphology of TiO2/in situ polymerized P3HT film was investigated by AFM in the contact mode. The short-circuit current density and energy conversion efficiencies of device with in situ polymerized P3HT layer were higher by 6 times and 3 times compared to that of device without the in situ polymerized P3HT layer. By adding poly (ethylene dioxythiophene)-poly (styrene sulfonic acid)(PEDOT-PSS) layer under the top contact, device showed a short-circuit current density of 1.27 mA cm−2, an open-circuit voltage of 0.52 V, a fill factor of 0.24, and a energy conversion efficiency of 0.16% at AM 1.5 solar illumination (100 mW cm−2).