Influence of TiN Inclusions on the Cleavage Fracture Behavior of Low-Carbon Microalloyed Steels

Toughness is a major concern for low-carbon microalloyed steels. In this work, the impact fracture behavior of two low-carbon Ti-V microalloyed steels was investigated in order to better understand the role of TiN inclusions in the toughness of the steels. The steels had similar chemical compositions and were manufactured by the same rolling process. However, there was an obvious difference in the ductile brittle transition temperature (DBTT) in the Charpy V-notch (CVN) impact tests of the two steels; one (steel 1) possessing a DBTT below −20 °C, while the DBTT of the other (steel 2) was above 15 °C. Scanning electron microscopy (SEM) fractography revealed that there were TiN inclusions at the cleavage fracture initiation sites on the fracture surfaces of steel 2 at both low and room temperatures. It is shown that the TiN inclusions had nucleated on Al₂O₃ particles and that they had pre-existing interior flaws. A high density of TiN inclusions was found in steel 2, but there was a much lower density in steel 1. Analysis indicates that these inclusions were responsible for the shift of DBTT to a higher temperature in steel 2. A mechanism is proposed for understanding the effect of the size and density of TiN inclusions on the fracture behavior, and the cleavage fracture initiation process is analyzed in terms of the distribution and development of stresses ahead of the notch tip during fracture at both low and room temperatures.