Investigation on strengthening of 7075 aluminum alloy sheet in a new hot stamping process with pre-cooling

verfasst von: Lijuan Zhu, Zhaoxiang Liu, Zhiqiang Zhang

Erschienen in: The International Journal of Advanced Manufacturing Technology | Ausgabe 9-12/2019

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

Hot stamping (HS) process is a new technology for fabricating high-strength aluminum alloy. In order to improve the formability of materials in the forming process, a new hot stamping process with pre-cooling (HSPC) is proposed in this paper. By adding a pre-cooling stage between the solid solution and the forming, the strain hardening exponent (SHE) could be increased due to the decreasing of the forming temperature, and the uniform deformation ability could be improved. In the HSPC of 7075 aluminum alloy, the blanks exhibited two pre-cooling modes: air cooling pre-cooling (ACPC) and cold iron pre-cooling (CIPC). The effects of pre-cooling rate and temperature on the microstructure and mechanical properties of formed parts were studied. The results showed that when the pre-cooling temperature was 300 °C by CIPC, the formed parts had the smallest thickness thinning and the best mechanical properties after aging. Compared with ACPC, CIPC had less precipitation during quenching, which ensured good subsequent aging strengthening effect.

Vorheriger Artikel Study on cutting performance of diamond-coated rhombic milling cutter in machining carbon fiber composites

Nächster Artikel Reduction in process-induced shape distortion of C-shaped composite parts using micro silica particles

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Muraoka Y, Miyaoka H (1993) Development of an all-aluminum automotive body. J Mater Process Technol 38(4):655–674CrossRef

Hirsch J (2011) Aluminium in innovative light-weight car design. J Mater Trans 52:818–824CrossRef

Chen G, Chen M, Wang N, Sun J (2016) Hot forming process with synchronous cooling for AA2024 aluminum alloy and its application. Int J Adv Manuf Technol 86(1-4):133–139CrossRef

Wei HQ (2007) Concurrent design process analysis and optimization for aluminum profile extrusion product development. Int J Adv Manuf Technol 33(7-8):652–661CrossRef

Novotny S, Geiger M (2003) Process design for hydroforming of lightweight metal sheets at elevated temperatures. J Mater Process Technol 138(1-3):594–599CrossRef

Toros S, Ozturk F, Kacar I (2008) Review of warm forming of aluminum–magnesium alloys. J Mater Process Technol 207(1-3):1–12CrossRef

He ZB, Fan XB, Xu YC, Yuan SJ (2011) Investigation on the formability of 5A06 sheet for rapid gas forming. Rare Metal Mater Eng 40:144–147

Zhang C, Yang S, Wang C, Zhao G, Gao A, Wang L (2016) Numerical and experimental investigation on thermo-mechanical behavior during transient extrusion process of high-strength 7××× aluminum alloy profile. Int J Adv Manuf Technol 85(5-8):1915–1926CrossRef

Liu Y, Zhu Z, Wang Z, Zhu B, Wang Y, Zhang Y (2018) Flow and friction behaviors of 6061 aluminum alloy at elevated temperatures and hot stamping of a B-pillar. Int J Adv Manuf Technol 96(9-12):4063–4083CrossRef

10.

Garrett RP, Lin J, Dean TA (2005) Solution heat treatment and cold die quenching in forming AA 6xxx sheet components: feasibility study. Adv Mater Res 6:673–680CrossRef

11.

Lin J, Dean T, Garrett R, Foster A (2008) Process for forming metal alloy sheet components. Patent WO2008059242A2

12.

Poole WJ, Sæter JA, Skjervold S, Waterloo G (2000) A model for predicting the effect of deformation after solution treatment on the subsequent artificial aging behavior of AA7030 and AA7108 alloys. Metall Mater Trans A 31(9):2327–2338CrossRef

13.

Tolouei R, Titheridge H (2009) Vehicle mass as a determinant of fuel consumption and secondary safety performance. Transp Res D 14(6):385–399CrossRef

14.

Molladavoudi HR, Djavanroodi F (2011) Experimental study of thickness reduction effects on mechanical properties and spinning accuracy of aluminum 7075-O, during flow forming. Int J Adv Manuf Technol 52(9-12):949–957CrossRef

15.

Zhao K, Chang Y, Hu P, Wu Y (2016) Influence of rapid cooling pretreatment on microstructure and mechanical property of hot stamped AHSS part. J Mater Process Technol 228:68–75CrossRef

16.

Chang Y, Meng ZH, Liang YI, Li XD, Ma N, Hu P (2011) Influence of hot press forming techniques on properties of vehicle high strength steels. J Iron Steel Res Int 18(5):59–63CrossRef

17.

Merklein M (2007) Mechanical properties and plastic anisotropy of the quenchenable high strength steel 22MnB5 at elevated temperatures. Key Eng Mater 344:79–86CrossRef

18.

Lin YC, Li LT, Fu YX, Jiang YQ (2012) Hot compressive deformation behavior of 7075 Al alloy under elevated temperature. J Mater Sci 47(3):1306–1318CrossRef

19.

Nélias D, Jullien JF, Wagan AI (2010) Thermo-mechanical characterisation of AA 6056-T4 and estimation of its material properties using Genetic Algorithm. Mater Des 31(9):4302–4311CrossRef

20.

Milkereit B, Kessler O, Schick C (2009) Recording of continuous cooling precipitation diagrams of aluminium alloys. Thermochim Acta 492(1-2):73–78CrossRef

21.

Schumacher P, Pogatscher S, Starink MJ, Schick C, Mohles V, Milkereit B (2015) Quench-induced precipitates in Al–Si alloys: calorimetric determination of solute content and characterisation of microstructure. Thermochim Acta 602:63–73CrossRef

22.

ASM Handbook Committee (1999) ASM Handbook Volume 4 Heat Treating. ASM International, Ohio

23.

Deschamps A, Brechet Y (1998) Nature and distribution of quench-induced precipitation in an Al-Zn-Mg-Cu alloy. Scr Mater 39(11):1517–1522CrossRef

24.

Fine ME (1975) Precipitation hardening of aluminum alloys. Metall Trans A 6(4):625–631CrossRef

25.

Stiller K, Warren PJ, Hansen V, Angenete J, Gjønnes J (1999) Investigation of precipitation in an Al–Zn–Mg alloy after two-step ageing treatment at 100 and 150 C. Mater Sci Eng A 270(1):55–63CrossRef

26.

Dehghani K, Ghorbani R, Soltanipoor AR (2015) Microstructural evolution and mechanical properties during the friction stir welding of 7075-O aluminum alloy. Int J Adv Manuf Technol 77(9-12):1671–1679CrossRef

27.

Dixit M, Mishra RS, Sankaran KK (2008) Structure–property correlations in Al 7050 and Al 7055 high-strength aluminum alloys. Mater Sci Eng A 478(1-2):163–172CrossRef

28.

Godard D, Archambault P, Aeby-Gautier E, Lapasset G (2002) Precipitation sequences during quenching of the AA 7010 alloy. Acta Mater 50(9):2319–2329CrossRef

29.

Ghosh A, Ghosh M, Shankar G (2018) On the role of precipitates in controlling microstructure and mechanical properties of Ag and Sn added 7075 alloys during artificial ageing. Mater Sci Eng A 738:399–411CrossRef

30.

Liu J, Yao P, Zhao N, Li X, Yang S (2016) Effect of minor Sc and Zr on recrystallization behavior and mechanical properties of novel Al–Zn–Mg–Cu alloys. J Alloys Compd 657:717–725CrossRef

31.

Lin L, Liu Z, Liu W, Zhou Y, Huang T (2018) Effects of Ag addition on precipitation and fatigue crack propagation behavior of a medium-strength Al–Zn–Mg Alloy. J Mater Sci Technol 34(3):534–540CrossRef

Titel: Investigation on strengthening of 7075 aluminum alloy sheet in a new hot stamping process with pre-cooling
verfasst von: Lijuan Zhu
Zhaoxiang Liu
Zhiqiang Zhang
Publikationsdatum: 14.06.2019
Verlag: Springer London
Erschienen in: The International Journal of Advanced Manufacturing Technology / Ausgabe 9-12/2019
Print ISSN: 0268-3768
Elektronische ISSN: 1433-3015
DOI: https://doi.org/10.1007/s00170-019-03890-0

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht

Springer Professional

Abstract

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Springer Professional "Technik"

Weitere Artikel der Ausgabe 9-12/2019

Theoretical and experimental investigation of a tool path control strategy for uniform surface generation in ultra-precision grinding

Research on forming characteristic of pulsed selective laser melting

A hybrid approach for measurement thickness of complex structural parts using ultrasonic inspection and on-machine probing

Feasibility study of manufacturing microgrooves on beryllium with electrochemical machining

Tool path generation for the point-pressing-based 5-axis CNC incremental forming

Multi-level simulation concept for multidisciplinary analysis and optimization of production systems

Premium Partner

Marktübersichten