Is adhesion between amorphous polymers sensitive to the bulk glass transition?

Two bulk samples of one and the same or of different amorphous polymers were brought into contact and held for a chosen period of time at a constant healing temperature (T) over the interval of T from below the bulk glass transition temperature (T _g ^bulk) by ~50 °C to above T _g ^bulk by ~10 °C. As formed adhesive joints were shear-fractured in tension at room temperature, and lap-shear strength (σ) was measured as a function of T. It has been found that σ develops with T as logσ ~ 1/T both at symmetric and asymmetric interfaces of polystyrene, poly (methyl methacrylate) and poly (2,6-dimethyl-1,4-phenylene oxide). This behaviour implies that there is no discontinuity in the evolution of σ when going through T _g ^bulk, and that this process is controlled by one and the same diffusion mechanism both below and above T _g ^bulk. The results obtained indicate that the contact layer of the polymers investigated is in the viscoelastic state at T well below T _g ^bulk and support the concept of a decrease in the T _g of a near-surface layer with respect to T _g ^bulk.