Magnetization study of Fe-doped ZnO co-doped with Cu: Synthesized by wet chemical method

Fe- and Cu-doped ZnO of nominal compositions Zn_0.95Fe_0.05O and Zn_0.94Fe_0.05Cu_0.01O were synthesized by a wet chemical route. X-ray diffraction analysis of the samples annealed at 575 K showed that they are single phase without any secondary phases. DC magnetization measurements of Cu co-doped samples (Zn_0.94Fe_0.05Cu_0.01O) as a function of field at room temperature showed ferromagnetic signature while the samples without Cu co-doping (Zn_0.95Fe_0.05O) are paramagnetic in nature. On increasing the temperature of annealing from 575 K to 1,075 K an impurity phase emerges in both the samples, which has been identified as a variant of ZnFe₂O₄. Both the samples heated at and above 1,075 K are found to be paramagnetic at room temperature. These observations, the absence of room temperature ferromagnetism in Zn_0.95Fe_0.05O and the disappearance of ferromagnetism in Zn_0.94Fe_0.05Cu_0.01O on raising the temperature of annealing clearly rules out the likelihood of room temperature ferromagnetism arising from the impurity phases like γ-Fe₂O₃ and/or ZnFe₂O₄ that might have been formed during the synthesis. Our results strongly suggest that room temperature ferromagnetism in Zn_0.94Fe_0.05Cu_0.01O can be attributed to the formation of a secondary phase of Cu-doped ZnFe₂O₄.