Thermal stability of heat-treated flame-synthesized anatase TiO₂ nanoparticles

In this article, TiO₂ nanoparticles were synthesized by using O₂-enriched coflow, hydrogen, diffusion flames. We investigated the thermal stability of the flame-synthesized TiO₂ nanoparticles by examining the crystalline structures of the nanoparticles and by analyzing the photocatalytic degradations of methylene blue solutions. Also, the results were compared with those of commercial P-25 nanoparticles. The maximum centerline temperature of the flame was measured to be 1,743 °C. Under this synthesis condition, TiO₂ nanoparticles, which were spherical with diameters approximately ranging from 30 to 60 nm, were synthesized. From the XRD analyses, about 96 wt.% of the synthesized nanoparticles were anatase-phase. After the heat-treatment at 800 °C for 30 min, the synthesized TiO₂ nanoparticles showed no significant changes of their shapes and crystalline phases. On the other hand, most of the commercial particles sintered with each other and changed to the rutile-phase. Whereas the photocatalytic ability of heat-treated commercial particles deteriorated, that of the flame-synthesized particles improved. On the basis of the improved result of photocatalytic degradation of methylene blue by using the heat-treated flame-synthesized nanoparticles, it is believed that the flame-synthesized TiO₂ nanoparticles have higher thermal stability at 800 °C than the commercial particles.