01.05.2010

Effects of heat treatment process and niobium addition on the microstructure and mechanical properties of low carbon steel weld metal

verfasst von: Shanping Lu, Shitong Wei, Dianzhong Li, Yiyi Li

Erschienen in: Journal of Materials Science | Ausgabe 9/2010

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

The mechanical properties and microstructure were evaluated and analyzed by optical microscopy (OM) and transmission electron microscopy (TEM) for micro-alloy carbon steel weld metal with and without Nb addition, respectively, under different heat treatment processes including stress relief annealing, normalizing, and no treatment after welding. The strength and elongation of the weld metal without treatment after welding were improved with the addition of Nb element, and the impact toughness was not affected obviously with the Nb addition. After stress relief annealing, the strength decreased for the Nb-free weld metal, while the elongation and impact toughness increased. However, for the Nb-bearing weld metal, stress relief annealing improved the strength of the weld metal significantly, and deteriorated the elongation and impact toughness. In the case of normalizing treatment to the weld metal, it was shown that with the increase of the holding time at the normalizing temperature of 920 °C, for both the weld metals with and without Nb addition, the microstructure of the columnar grain zone (CGZ) was transformed from one of columnar grain into one of equiaxed grain. The grain size of the equiaxed grain zone (EGZ) increased initially, then remained almost unchanged with the prolonging of the holding time. The mechanical properties of the weld metal with and without Nb addition showed no obvious change with the increasing holding time. With the increase of the normalizing temperature, the strength of the Nb-bearing weld metal increased, while the elongation and impact toughness decreased significantly. OM and TEM analysis found that the fine NbC particles were precipitated at the normalizing temperature of 920 °C, which refined the grains of the weld metal and increased the impact toughness. With the increase of the normalizing temperature, the content of widmanstatten ferrite (WF) in the Nb-bearing weld metal increased, whereas the quantity of the NbC particles decreased, which improved the strength and lowered the impact toughness.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
2.
Zurück zum Zitat Pereloma EV, Timokhina IB, Russell KF, Miller MK (2006) Scr Mater 54:471CrossRef Pereloma EV, Timokhina IB, Russell KF, Miller MK (2006) Scr Mater 54:471CrossRef
4.
Zurück zum Zitat Thridandapani RR, Misra RDK, Mannering T, Panda D, Jansto S (2006) Mater Sci Eng A 422:285CrossRef Thridandapani RR, Misra RDK, Mannering T, Panda D, Jansto S (2006) Mater Sci Eng A 422:285CrossRef
7.
8.
Zurück zum Zitat Shanmugam S, Misra RDK, Hartmann J, Jansto SG (2006) Mater Sci Eng A 441:215CrossRef Shanmugam S, Misra RDK, Hartmann J, Jansto SG (2006) Mater Sci Eng A 441:215CrossRef
9.
10.
Zurück zum Zitat Shanmugam S, Ramisetti NK, Misra RDK, Mannering T, Panda D, Jansto S (2007) Mater Sci Eng A 460–461:335 Shanmugam S, Ramisetti NK, Misra RDK, Mannering T, Panda D, Jansto S (2007) Mater Sci Eng A 460–461:335
11.
Zurück zum Zitat Anumolu R, Ravi Kumar B, Misra RDK, Mannering T, Panda D, Jansto SG (2008) Mater Sci Eng A 491:55CrossRef Anumolu R, Ravi Kumar B, Misra RDK, Mannering T, Panda D, Jansto SG (2008) Mater Sci Eng A 491:55CrossRef
12.
Zurück zum Zitat Shanmugam S, Ramisetti NK, Misra RDK, Hartmann J, Jansto SG (2008) Mater Sci Eng A 478:26CrossRef Shanmugam S, Ramisetti NK, Misra RDK, Hartmann J, Jansto SG (2008) Mater Sci Eng A 478:26CrossRef
13.
14.
Zurück zum Zitat Shanmugam S, Misra RDK, Mannering T, Panda D, Jansto SG (2006) Mater Sci Eng A 437:436CrossRef Shanmugam S, Misra RDK, Mannering T, Panda D, Jansto SG (2006) Mater Sci Eng A 437:436CrossRef
15.
Zurück zum Zitat Pereloma EV, Timokhina IB, Hodgson PD (1999) Mater Sci Eng A 273–275:448 Pereloma EV, Timokhina IB, Hodgson PD (1999) Mater Sci Eng A 273–275:448
16.
Zurück zum Zitat Nayak SS, Misra RDK, Hartmann J, Siciliano F, Gray JM (2008) Mater Sci Eng A 494:456CrossRef Nayak SS, Misra RDK, Hartmann J, Siciliano F, Gray JM (2008) Mater Sci Eng A 494:456CrossRef
17.
Zurück zum Zitat Shiga C, Gotoh A, Kojima T, Horii Y, Fukada Y, Ikeuti K, Matuda F (1996) Weld World 37:163 Shiga C, Gotoh A, Kojima T, Horii Y, Fukada Y, Ikeuti K, Matuda F (1996) Weld World 37:163
18.
Zurück zum Zitat Billy J, Johansson T, Loberg B, Easterling KE (1980) Met Technol 7:67 Billy J, Johansson T, Loberg B, Easterling KE (1980) Met Technol 7:67
20.
Zurück zum Zitat Farrar RA, Taylor LG, Harrison EM (1979) Met Technol 6:380 Farrar RA, Taylor LG, Harrison EM (1979) Met Technol 6:380
21.
Zurück zum Zitat Garland JG, Kirkwood PR (1975) Met Constr 7:275 Garland JG, Kirkwood PR (1975) Met Constr 7:275
22.
Zurück zum Zitat Farrar RA, Wong SY, Watson MNW (1980) Weld Met Fabr 48:21 Farrar RA, Wong SY, Watson MNW (1980) Weld Met Fabr 48:21
23.
24.
Zurück zum Zitat Garland JG, Kirkwood PR (1975) Met Constr 7:320 Garland JG, Kirkwood PR (1975) Met Constr 7:320
25.
Zurück zum Zitat Yi HL, Du LX, Wang GD, Liu XH (2005) J Mater Metall 4:295 (In Chinese) Yi HL, Du LX, Wang GD, Liu XH (2005) J Mater Metall 4:295 (In Chinese)
27.
28.
Zurück zum Zitat Hong SC, Lim SH, Hong HS, Lee KJ, Shin DH, Lee KS (2003) Mater Sci Eng A 355:241CrossRef Hong SC, Lim SH, Hong HS, Lee KJ, Shin DH, Lee KS (2003) Mater Sci Eng A 355:241CrossRef
29.
Zurück zum Zitat Li Y, Wilson JA, Crowther DN, Mitchell PS, Craven AJ, Baker TN (2004) ISIJ Int 44:1093CrossRef Li Y, Wilson JA, Crowther DN, Mitchell PS, Craven AJ, Baker TN (2004) ISIJ Int 44:1093CrossRef
Metadaten
Titel
Effects of heat treatment process and niobium addition on the microstructure and mechanical properties of low carbon steel weld metal
verfasst von
Shanping Lu
Shitong Wei
Dianzhong Li
Yiyi Li
Publikationsdatum
01.05.2010
Verlag
Springer US
Erschienen in
Journal of Materials Science / Ausgabe 9/2010
Print ISSN: 0022-2461
Elektronische ISSN: 1573-4803
DOI
https://doi.org/10.1007/s10853-010-4205-1

Weitere Artikel der Ausgabe 9/2010

Journal of Materials Science 9/2010 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.