Fabrication of an aluminum–carbon nanotube metal matrix composite by accumulative roll-bonding

verfasst von: S. Salimi, H. Izadi, A. P. Gerlich

Erschienen in: Journal of Materials Science | Ausgabe 2/2011

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

Accumulative roll-bonding was adapted to fabricate a carbon nanotube (CNT)-reinforced aluminum matrix composite. Its microstructure was investigated by transmission electron microscopy, and it was confirmed that the nanotubes were embedded into the metal matrix while maintaining their multiwalled structure. Measurements revealed that the as-received CNTs had a bimodal diameter size distribution, while only nanotubes with diameters >30 nm and >30 walls were retained during four consecutive rolling operations at 50% reduction.

Vorheriger Artikel Influence of hybrid organic–inorganic sol–gel matrices on the photophysics of amino-functionalized UV-sensitizers

Nächster Artikel Preparation and photoelectrochemical characterization of WO3/TiO2 nanotube array electrode

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Saito Y, Utsunomiya H, Tsuji N, Sakai T (1999) Acta Mater 47:579CrossRef

Vaidyanath LR, Nicholas MG, Milner DR (1959) Br Weld J 6:13

Tsuji N, Saito Y, Lee SH, Minamino Y (2003) Adv Eng Mater 5:338CrossRef

Saito Y, Tsuji N, Utsunomiya H, Sakai T, Hong RG (1998) Scripta Mater 39:1221CrossRef

Tsuji N, Saito Y, Utsunomiya H, Tanigawa S (1999) Scripta Mater 40:795CrossRef

Hsieh PJ, Lo YC, Huang JC, Ju SP (2006) Intermetallics 14:924CrossRef

Min GH, Lee JM, Kang SB, Kim HW (2006) Mater Lett 60:3255CrossRef

Dinda GP, Rosner H, Wilde G (2005) Scripta Mater 52:577CrossRef

Mizuuchi K, Inoue K, Yamauchi K, Enami K, Itami M, Okanda Y (2001) Mater Sci Eng A Struct 316:93CrossRef

10.

Lu C, Tieu K, Wexler D (2009) J Mater Process Technol 209:4830CrossRef

11.

Li YH, Housten W, Zhao YM et al (2007) Nanotechnology 18(20), Article No. 205607

12.

Lahiri D, Bakshi SR, Keshri AK, Liu Y, Agarwal A (2009) Mater Sci Eng A Struct 523:263CrossRef

13.

Iijima S, Brabec C, Maiti A, Bernholc J (1996) J Chem Phys 104:2089CrossRef

14.

Falvo MR, Clary GJ, Taylor RM et al (1997) Nature 389:582CrossRef

15.

Kwon H, Park DH, Silvain JF, Kawasaki A (2010) Compos Sci Technol 70:546CrossRef

16.

Iijima S (1991) Nature 354:56CrossRef

17.

Treacy MMJ, Ebbesen TW, Gibson JM (1996) Nature 381:678CrossRef

18.

Ruoff RS, Lorents DC (1995) Carbon 33:925CrossRef

19.

Takesue I, Haruyama J, Kobayashi N et al (2006) Phys Rev Lett 96(5), Article No. 057001

20.

Quang P, Jeong YG, Yoon SC, Hong SH, Kim HS (2007) J Mater Process Technol 187:318CrossRef

21.

Salas W, Alba-Baena NG, Murr LE (2007) Metall Mater Trans A 38A:2928CrossRef

22.

Morsi K, Esawi A (2007) J Mater Sci 42:4954. doi:10.1007/s10853-006-0699-y CrossRef

23.

Kuzumaki T, Miyazawa K, Ichinose H, Ito K (1998) J Mater Res 13:2445CrossRef

24.

Zhong R, Cong HT, Hou PX (2003) Carbon 41:848CrossRef

25.

Noguchi T, Magario A, Fukazawa S, Shimizu S, Beppu J, Seki M (2004) Mater Trans 45:602CrossRef

26.

Esawi AMK, El Borady MA (2008) Compos Sci Technol 68:486CrossRef

27.

Ci LJ, Ryu ZY, Jin-Phillipp NY, Ruhle M (2006) Acta Mater 54:5367CrossRef

28.

Pirgazi H, Akbarzadeh A, Petrov R, Sidor J, Kestens L (2008) Mater Sci Eng A Struct 492:110CrossRef

29.

Valiev RZ, Chmelik F, Bordeaux F, Kapelski G, Baudelet B (1992) Scripta Metall Mater 27:855CrossRef

30.

Kamikawa N, Tsuji N, Huang XX, Hansen N (2006) Acta Mater 54:3055CrossRef

31.

Tsuji N, Saito Y, Ito Y et al (2000) In: Symposium on ultrafine grained materials at the 2000TMS annual meeting, Mar 12–16, 2000, Nashville, TN, Ultrafine Grained Materials, pp 207–218

32.

Ito Y, Tsuji N, Saito Y, Utsunomiya H, Sakai T (2000) J Jpn Inst Met 64:429

33.

Lee SH, Saito Y, Tsuji N, Utsunomiya H, Sakai T (2002) Scripta Mater 46:281CrossRef

34.

Kamikawa N, Sakai T, Tsuji N (2007) Acta Mater 55:5873CrossRef

35.

Tsuji N, Ueji R, Ito Y, Saito Y (2000) In: Proceedings of the 21st RISØ international symposium on material science, p 607

36.

Ashby MF (1970) Philos Mag 21:399CrossRef

37.

Iwahashi Y, Horita Z, Nemoto M, Langdon TG (1998) Acta Mater 46:3317CrossRef

38.

Keller TM, Laskoski M, Osofsky M, Qadri SB (2008) Phys Status Solidi A Appl Mater Sci 205:1585CrossRef

39.

Willems I, Konya Z, Colomer JF et al (2000) Chem Phys Lett 317:71CrossRef

40.

Hertel T, Walkup RE, Avouris P (1998) Phys Rev B 58:13870CrossRef

41.

Wang CY, Mioduchowski A (2007) J Appl Phys 101(1), Article No. 014306

42.

Shen HS, Zhang CL (2007) Int J Solids Struct 44:1461CrossRef

43.

Deck CP, Flowers J, McKee GSB et al (2007) J Appl Phys 101(2), Article No. 023512

44.

Tang DS, Chen LC, Wang LJ et al (2000) J Mater Res 15:560CrossRef

Titel: Fabrication of an aluminum–carbon nanotube metal matrix composite by accumulative roll-bonding
verfasst von: S. Salimi
H. Izadi
A. P. Gerlich
Publikationsdatum: 01.01.2011
Verlag: Springer US
Erschienen in: Journal of Materials Science / Ausgabe 2/2011
Print ISSN: 0022-2461
Elektronische ISSN: 1573-4803
DOI: https://doi.org/10.1007/s10853-010-4855-z

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht

Springer Professional

Abstract

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Springer Professional "Technik"

Weitere Artikel der Ausgabe 2/2011

Shear-thickening behaviour of concentrated polymer dispersions under steady and oscillatory shear

The effects of calcium and yttrium additions on the microstructure, mechanical properties and biocompatibility of biodegradable magnesium alloys

C–S–H/polyaniline nanocomposites prepared by in situ polymerization

Alkaline hydrothermal kinetics in titanate nanostructure formation

Toughening of epoxy using core–shell particles

Phase constituents and thermal expansion behavior of a NiCrAlYRe coating alloy

Premium Partner

Marktübersichten