Activation energy of poly(methyl methacrylate) from rheometry and polymer welding
Erschienen in: Journal of Materials Science | Ausgabe 13/2011
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
In this article, activation energies for a poly(methyl methacrylate) material were determined by shear rheometry and by bond strength in welding. Functions for temperature dependency of viscosity and for bond strength, depending on time and temperature, were found. These functions were fitted to measurements from shear rheometry between 230 and 270 °C and from strength of lap-shear joints welded from 105 to 130 °C, where by values of activation energies were found. It was found that bonding pressure was less than significant. Despite experimental differences, there was good correlation with data from literature for each method as well as for temperature dependency.