Hardness and fracture toughness of thermoelectric La_3−xTe₄

verfasst von: James M. Ma, Samad A. Firdosy, Richard B. Kaner, Jean-Pierre Fleurial, Vilupanur A. Ravi

Erschienen in: Journal of Materials Science | Ausgabe 3/2014

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

Lanthanum telluride (La_3−xTe₄) is a state-of-the-art n-type high temperature thermoelectric material that behaves as a weak and brittle ceramic. Vickers microindentation hardness testing was explored as a rapid analysis technique to characterize the mechanical properties of this material. An indentation size effect was observed with hardness values ranging from 439 ± 31 kgf/mm² (0.01 kgf/10 s contact time) to 335 ± 6 kgf/mm² (0.5 kgf/10 s contact time). The Vickers indentation fracture toughness, K _VIF, based on measurements of crack lengths emanating from the corners of the Vickers indents was 0.70 ± 0.06 MPa m^1/2.

Vorheriger Artikel One-pot synthesis of carbon nanotubes from renewable resource: cellulose acetate

Nächster Artikel The quaternary Al–Fe–Ni–Si phase equilibria in Al-rich corner: experimental measurement and thermodynamic modeling

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Yang J, Caillat T (2006) MRS Bull J 31:224CrossRef

Fleurial J-P (2009) J Manag 61:79. doi:10.1007/s11837-009-0057-z

Snyder GJ, Toberer ES (2008) Nat Mater 7:105PubMedCrossRefADS

ASTM (2010) ASTM Standard, ASTM C1421 - 10 standard test methods for determination of fracture toughness of advanced ceramics at ambient temperature. doi: 10.1520/C1421-10

ASTM (2011) ASTM Standard, ASTM E1820 - 11 standard test method for measurement of fracture toughness. doi: 10.1520/E1820-11

ASTM (2002) ASTM Standard, ASTM C1211 - 02 standard test method for flexural strength of advanced ceramics at elevated temperatures

ASTM (2009) ASTM Standard, ASTM C 1499-09 standard test method for monotonic equibiaxial flexural strength of advanced ceramics at ambient temperature

Gladden JR, Li G, Adebisi R et al (2010) Phys Rev B 82:1. doi:10.1103/PhysRevB.82.045209

Duan B, Zhai P, Wen P, Zhang S (2012) Scr Mater 67:372. doi:10.1016/j.scriptamat.2012.05.028 CrossRef

10.

Ueno K, Yamamoto A, Noguchi T et al (2004) J Alloy Compd 384:254CrossRef

11.

Ueno K, Yamamoto A, Noguchi T et al (2005) Mech Prop 388:118. doi:10.1016/j.jallcom.2004.07.005

12.

Ueno K, Yamamoto A, Noguchi T et al (2005) J Alloy Compd 392:295. doi:10.1016/j.jallcom.2004.08.078 CrossRef

13.

Ravi V, Firdosy S, Caillat T et al (2008) AIP Conf Proc 969:656. doi:10.1063/1.2845027 CrossRefADS

14.

Firdosy SA, Ravi VA, Li B et al (2013) In: 11th international energy conversion engineering conference. doi:10.2514/6.2013-3929

15.

Palmqvist S (1957) Jernkontorets Ann 141:300

16.

Palmqvist S (1962) Arch Eisenhuettenwes 33:629

17.

Palmqvist S (1963) Jernkontorets Ann 147:107

18.

Lawn B, Wilshaw R (1975) J Mater Sci 10:1049. doi:10.1007/BF00823224 CrossRefADS

19.

Lawn BR, Swain MV (1975) J Mater Sci 10:113. doi:10.1007/BF00541038 CrossRefADS

20.

Lawn BR, Fuller ER (1975) J Mater Sci 10:2016. doi:10.1007/BF00557479 CrossRefADS

21.

Evans AG (1979) In: Proceedings of the 11th National Symposium on fracture mechanics: Part II. ASTM, pp 112–135

22.

Lankford J (1982) J Mater Sci Lett 1:493CrossRef

23.

Spiegler R, Schmauder S, Sigl LS (1990) J Hard Mater 1:147

24.

Shetty DK, Wright IG, Mincer PN, Clauer AH (1985) J Mater Sci 20:1873. doi:10.1007/BF00555296 CrossRefADS

25.

Niihara K (1983) J Mater Sci Lett 2:221CrossRef

26.

Gilman JJ (2009) Chemistry and physics of mechanical hardness. Wiley-Interscience, HobokenCrossRef

27.

Evans AG, Charles EA (1976) J Am Ceram Soc 59:371. doi:10.1111/j.1151-2916.1976.tb10991.x CrossRef

28.

Zhao L-D, Zhang B-P, Li J-F et al (2008) J Alloy Compd 455:259. doi:10.1016/j.jallcom.2007.01.015 CrossRef

29.

Ren F, Ni JE, Case ED, et al. (2007) MRS Proceedings. doi: 10.1557/PROC-1044-U04-04

30.

May A, Fleurial J, Snyder G (2008) Phys Rev B 78:1. doi:10.1103/PhysRevB.78.125205

31.

ASTM (2010) ASTM Standard, ASTM E122-10 standard test methods for determining average grain size

32.

Ponton C, Rawlings R (1989) Mater Sci Technol 5:961CrossRef

33.

Cox WL, Steinfink H, Bradley WF (1965) Inorg Chem 5:318CrossRef

34.

ASTM (2008) ASTM Standard, ASTM C1327 - 08 standard test method for vickers indentation hardness of advanced ceramics. doi: 10.1520/C1327-08

35.

Ren F, Case ED, Timm EJ, Schock HJ (2008) J Alloy Compd 455:340. doi:10.1016/j.jallcom.2007.01.086 CrossRef

36.

Crocker AJ, Wilson M (1978) J Mater Sci 13:833. doi:10.1007/BF00570520 CrossRefADS

37.

Rogl G, Rogl P (2011) Sci Adv Mater 3:517. doi:10.1166/sam.2011.1181 CrossRef

38.

Kallel AC, Roux G, Martin CL (2013) Mater Sci Eng A 564:65CrossRef

39.

Pharr GM, Herbert EG, Gao Y (2010) Annu Rev Mater Res 40:271. doi:10.1146/annurev-matsci-070909-104456 CrossRefADS

40.

Farges G, Degout D (1989) Thin Sol Films 181:365. doi:10.1016/0040-6090(89)90505-1 CrossRefADS

41.

Sangwal K (2009) Cryst Res Technol 44:1019. doi:10.1002/crat.200900385 CrossRef

42.

Gong J, Wu J, Guan Z (1999) J Eur Ceram Soc 19:2625CrossRef

43.

Shu JY, Fleck NA (1998) Int J Sol Struct 35:1363. doi:10.1016/S0020-7683(97)00112-1 CrossRefMATH

44.

Gerberich WW, Tymiak NI, Grunlan JC et al (2002) J Appl Mech 69:433. doi:10.1115/1.1469004 CrossRefMATH

45.

Gouldstone A, Chollacoop N, Dao M et al (2007) Acta Mater 55:4015. doi:10.1016/j.actamat.2006.08.044 CrossRef

46.

Lawn BR, Marshall DB (1979) J Am Ceram Soc 62:347CrossRef

47.

Quinn GD (2007) Fractography of ceramics and glasses. National Institute of Standards and Technology, Washington, DC

48.

Quinn GD, Bradt RC (2007) J Am Ceram Soc 680:673. doi:10.1111/j.1551-2916.2006.01482.x CrossRef

49.

Ponton C, Rawlings R (1989) Mater Sci Technol 5:865CrossRef

50.

Wiederhorn SM (1969) J Am Ceram Soc 1968:99CrossRef

51.

Ni JE, Case ED, Khabir KN et al (2010) Mater Sci Eng B 170:58. doi:10.1016/j.mseb.2010.02.026 CrossRef

Titel: Hardness and fracture toughness of thermoelectric La3−x Te4
verfasst von: James M. Ma
Samad A. Firdosy
Richard B. Kaner
Jean-Pierre Fleurial
Vilupanur A. Ravi
Publikationsdatum: 01.02.2014
Verlag: Springer US
Erschienen in: Journal of Materials Science / Ausgabe 3/2014
Print ISSN: 0022-2461
Elektronische ISSN: 1573-4803
DOI: https://doi.org/10.1007/s10853-013-7794-7

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht

Springer Professional

Abstract

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Springer Professional "Technik"

Weitere Artikel der Ausgabe 3/2014

Hot working behavior of a WE54 magnesium alloy

Effect of hollow sphere size and size distribution on the quasi-static and high strain rate compressive properties of Al-A380–Al2O3 syntactic foams

Kinetics of shrinkage and shape evolution during liquid phase sintering of tungsten heavy alloy

A microscale formaldehyde gas sensor based on Zn2SnO4/SnO2 and produced by combining hydrothermal synthesis with post-synthetic heat treatment

New chiral liquid crystalline monomers, polymers, and elastomers derived from menthol derivatives: synthesis and mesomorphism

Morphology and fracture toughness of nanostructured epoxy thermosets containing macromolecular miktobrushes composed of poly(ε-caprolactone) and polydimethylsiloxane side chains

Premium Partner

Marktübersichten