Synthesis and properties of amphiphilic thermo-sensitive block copolymers

Octadecyl acrylate (ODA) as hydrophobic monomer and N-isopropylacryamide (NIPAAm) as hydrophilic monomer were chosen to synthetize the thermo-sensitive block copolymers PODA_x-PNIPAAm_y-PODA_x (BAB-type) via reversible-addition-fragmentation chain transfer (RAFT) polymerization, the block copolymers could self-assemble to flower-like micelles in aqueous solution with hydrophobic PODA as the inner core and stabilized by hydrophilic PNIPAAm as the outer shell. The characterizations of the micelles such as surfactivity, thermo-sensitivity, micelle hydrodynamic radius (R _h ) and polydispersity index (PdI) were demonstrated by surface tension technique, UV-Vis, and dynamic light scattering (DLS) measurements, respectively. The longer the hydrophilic chain was, the higher the critical micellization concentration (CMC) would be, and the higher content of the PODA was, the lower the lower critical solution temperature (LCST) would be. The average R _h remained at about 100 nm below LCST, but decreased sharply to about 42 nm and kept constant when reaching and above LCST, which meant the non-aggregation of BAB type block copolymers. The micelle was homogeneous with the small PdI within the range of research. B_0.5mA_24mB_0.5m had the largest capacity to encapsulate lipophilic Sudan Red IV model drugs and the drug loading efficiency was 9.76%.