Dewatering Behaviour of a Uranium Ore Slurry Containing Clays

The main objective of this paper was to investigate the dewatering behaviour of a clayey uranium ore slurry. The slurry (containing 28% clay size) exhibited moderate water adsorption (w _l  = 83% and w _p  = 30%). Primarily composed of muscovite (46%) and quartz (30%), the clay minerals included illite (8%), chlorite (5%) and kaolinite (2%) alongside a CEC of 41 (cmol(+)/kg) with Ca²⁺ and Mg²⁺ as the dominant cations. Likewise, the high EC (17,600 μS/cm) and ionic strength (1.15 mol/L) indicated a flocculated microstructure due to the presence of SO₄ ²⁻ (22,600 mg/L) and Mg²⁺ (1340 mg/L) in the slurry water. Settling included sedimentation and consolidation at low initial solids condition (25–35%) whereas only consolidation was observed at high initial solids contents (40–50%). The average k reduced from 1.2 × 10⁻⁶ m/s (initial s = 25%) to 5.3 × 10⁻⁸ m/s (initial s = 50%) along with a void ratio reduction from 7.4 to 2.6. Due to thixotropic strength, volume compressibility during consolidation showed apparent pre-consolidation at low effective stress (0.3–2 kPa) with a reduction in void ratio from 2.6 to 2.5. The e _s was found to be 2.46 at σ′ = 2 kPa and was followed by a steeper slope with the void ratio reducing to 2.1 at σ′ = 31 kPa. Likewise, the hydraulic conductivity during consolidation decreased from 2.6 × 10⁻⁹ m/s (at e = 2.6) to 2.0 × 10⁻¹⁰ m/s (at e = 2.1).