Low temperature synthesis of calcium cobaltites in a solid state reaction

This paper presents synthesis of calcium cobaltites of the nominal composition of Ca₃Co₄O₉ prepared by the solid state reaction. The reaction between CaCO₃ and Co₃O₄ was investigated at 700–900 °C during 20 h and at 800 °C during 2–30 h. Mass changes, phase composition and Co⁺³, Co⁺⁴ content were examined. Stability of the calcined specimens was tested by DTA/TG. It was found that two phases: Ca₃Co₄O₉ and Ca₃Co₂O₆ were present as a result of calcinations above 800 °C. On the other hand, the temperature of 750 °C was too low for calcium cobaltites to be synthesized. Mono-phase material with Ca₃Co₄O₉ phase was obtained after calcinations at 800 °C but non-stoichiometry of the compound and its relation to the calcinations time were found. Once synthesized, the compound was stable up to 900 °C.