Piezoelectric properties and dielectric behavior of Bi_1/2Na_1/2[Ti_1−x (Sb_1/2Nb_1/2) _x ]O₃ lead-free piezoelectric ceramics

New lead-free piezoelectric ceramics of ABO₃ perovskite type, Bi_1/2Na_1/2[Ti_1−x (Sb_1/2Nb_1/2) _x ]O₃, were synthesized by conventional solid state reaction. The effect of the replacement of complex ions of (Sb_1/2Nb_1/2)⁴⁺ in the B cationic site on structural and electrical properties was investigated. The XRD analysis showed that all samples exhibited a single phase of perovskite structure. Piezoelectric and dielectric measurement revealed that the substitution of (Sb_1/2Nb_1/2)⁴⁺ ions lead to an increase in piezoelectric constant(d ₃₃), electromechanical coupling factor(k _t), relative dielectric constant(ɛ _r),and loss tangent (tanδ), while excess of (Nb_1/2Sb_1/2)⁴⁺ ions results in a decrease in d ₃₃, k _t, ɛ _r, but an increase in tanδ. Temperature dependence of dielectric constant ɛ _r measurement indicated these compounds were relaxor ferroelectric. At low frequency and high temperature, dielectric constant increased sharply attributed to the superparaelectric clusters after (Sb_1/2Nb_1/2)⁴⁺ ions substitution.