Synthesis and characterization of anatase and rutile TiO₂ nanorods by template-assisted method

verfasst von: A. Sadeghzadeh Attar, M. Sasani Ghamsari, F. Hajiesmaeilbaigi, Sh. Mirdamadi, K. Katagiri, K. Koumoto

Erschienen in: Journal of Materials Science | Ausgabe 17/2008

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

Well-aligned anatase and rutile TiO₂ nanorods and nanotubes with a diameter of about 80–130 nm have successfully been fabricated via sol-gel template method. The prepared samples were characterized by using thermogravimetric (TG) and differential thermal analysis (DTA), X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and energy dispersive X-ray spectroscopy (EDS). The XRD results indicated that the TiO₂ nanorods were crystallized in the anatase and rutile phases, after annealing at 400–800 °C for different periods of time from 0.2 to 10 h.

Vorheriger Artikel Combustion synthesis/quasi-isostatic pressing of TiC0.7–NiTi cermets: microstructure and transformation characteristics

Nächster Artikel Droplet cooling in atomization sprays

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Mulmi DD, Sekiya T, Kamiya N, Kurita S, Murakami Y, Kodaira T (2004) J Phys Chem Solids 65:1181. doi:https://doi.org/10.1016/j.jpcs.2003.12.009 CrossRef

Karvinen S, Hirva P, Pakkanen TA (2003) J Mol Struct Theochem 626:271. doi:https://doi.org/10.1016/S0166-1280(03)00108-8 CrossRef

Xu A-W, Gao Y, Liu H-Q (2002) J Catal 207:151. doi:https://doi.org/10.1006/jcat.2002.3539 CrossRef

Keshmiri M, Mohseni M, Troczynski T (2004) Appl Catal Environ 53:209. doi:https://doi.org/10.1016/j.apcatb.2004.05.016 CrossRef

Niederberger M, Bartl MH, Stucky GD (2002) Chem Mater 4:4364. doi:https://doi.org/10.1021/cm021203k CrossRef

Wang C-C, Ying JY (1999) Chem Mater 11:3113. doi:https://doi.org/10.1021/cm990180f CrossRef

Wang C, Deng Z-X, Li Y (2001) Inorg Chem 40:5210. doi:https://doi.org/10.1021/ic0101679 CrossRef

Kumar PM, Badrinarayanan S, Sastry M (2000) Thin Solid Films 358:122. doi:https://doi.org/10.1016/S0040-6090(99)00722-1 CrossRef

Sen S, Mahanty S, Roy S, Heintz O, Bourgeois S, Chaumont D (2005) Thin Solid Films 474:245. doi:https://doi.org/10.1016/j.tsf.2004.04.004 CrossRef

10.

Wu J-J, Yu C-C (2004) J Phys Chem B 108:3377. doi:https://doi.org/10.1021/jp0361935 CrossRef

11.

Ovenstone J, Yanagisawa K (1999) Chem Mater 11:2770. doi:https://doi.org/10.1021/cm990172z CrossRef

12.

Kolenko YV, Garshev AV, Churagulov BR, Boujday S, Portes P, Colbeau-Justin C (2005) J Photochem Photobiol Chem 172:19. doi:https://doi.org/10.1016/j.jphotochem.2004.11.004 CrossRef

13.

Djaoued Y, Bruning R, Bersani D, Lottici PP, Badilescu S (2004) Mater Lett 58:2618. doi:https://doi.org/10.1016/j.matlet.2004.03.034 CrossRef

14.

Banfi G, Degiorgio V, Ricard D (1998) Adv Phys 47:447. doi:https://doi.org/10.1080/000187398243537 CrossRef

15.

Shklover V, Nazeeruddin M-K, Zakeeruddin SM, Barbe C, Kay A, Haibach T et al (1997) Chem Mater 9:430. doi:https://doi.org/10.1021/cm950502p CrossRef

16.

Francioso L, Taurino AM, Forleo A, Siciliano P (2008) Sens Actuators B 130:70. doi:https://doi.org/10.1016/j.snb.2007.07.074 CrossRef

17.

Hong J, Cao J, Sun J, Li H, Chen H, Wang M (2003) Chem Phys Lett 380:366. doi:https://doi.org/10.1016/j.cplett.2003.09.037 CrossRef

18.

Zhang Z, Wang C-C, Zakaria R, Ying JY (1998) J Phys Chem B 102:10871. doi:https://doi.org/10.1021/jp982948± CrossRef

19.

Shipway AN, Katz E, Willner I (2000) ChemPhysChem 1:18. doi:10.1002/1439-7641(20000804)1:1<18::AID-CPHC18>3.0.CO;2-L CrossRef

20.

Wu Y, Yan H, Huang M, Messer B, Song JH, Yang P (2002) Chem Eur J 8:1260. doi:10.1002/1521-3765(20020315)8:6<1260::AID-CHEM1260>3.0.CO;2-Q CrossRef

21.

Boujday S, Wunsch F, Portes P, Bocquet J-F, Colbeau-Justin C (2004) Solar Energy Mater Solar Cells 83:421. doi:https://doi.org/10.1016/j.solmat.2004.02.035 CrossRef

22.

Jiu J, Isoda S, Wang F, Adachi M (2006) J Phys Chem B 110:2087. doi:https://doi.org/10.1021/jp055824n CrossRef

23.

Pradhan SK, Reucroft PJ, Yang F, Dozier A (2003) J Cryst Growth 256:83. doi:https://doi.org/10.1016/S0022-0248(03)01339-3 CrossRef

24.

Zhao X-M, Xia Y, Whitesides GM (1997) J Mater Chem 7:1069. doi:https://doi.org/10.1039/a700145b CrossRef

25.

Cozzoli PD, Kornowski A, Weller H (2003) J Am Chem Soc 125:14539. doi:https://doi.org/10.1021/ja036505h CrossRef

26.

Lakshmi BB, Dorhout PK, Martin CR (1997) Chem Mater 9:857. doi:https://doi.org/10.1021/cm9605577 CrossRef

27.

Zhang M, Bando Y, Wada K (2001) J Mater Sci Lett 20:167. doi:https://doi.org/10.1023/A:1006739713220 CrossRef

28.

Sadeghzadeh Attar A, Mirdamadi Sh, Hajiesmaeilbaigi F, Sasani Ghamsari M (2007) J Mater Sci Technol 23:611

29.

Sander M, Cote MJ, Gu W, Kile BM, Tripp CP (2004) Adv Mater 16:2052. doi:https://doi.org/10.1002/adma.200400446 CrossRef

30.

Mikhaylova M, Kim DK, Toprak M, Muhammed M (2003) Mat Res Soc Symp Proc 750:1

31.

Cullity BD (1978) Elements of X-ray diffraction. Addison Wesley Pub, Menlo Park

32.

Hong S-S, Lee MS, Park SS, Lee G-D (2003) Catal Today 87:99. doi:https://doi.org/10.1016/j.cattod.2003.10.012 CrossRef

33.

Diggle JW, Downie TC, Goulding C (1969) Chem Rev 69:365. doi:https://doi.org/10.1021/cr60259a005 CrossRef

34.

Yoon J-H, Jang S-R, Vittal R, Lee J, Kim K-J (2006) J Photochem Photobiol A: Chem 180:184. doi:https://doi.org/10.1016/j.jphotochem.2005.10.013 CrossRef

35.

Lakshmi BB, Patrissi CJ, Martin CR (1997) Chem Mater 9:2544. doi:https://doi.org/10.1021/cm970268y CrossRef

Titel: Synthesis and characterization of anatase and rutile TiO2 nanorods by template-assisted method
verfasst von: A. Sadeghzadeh Attar
M. Sasani Ghamsari
F. Hajiesmaeilbaigi
Sh. Mirdamadi
K. Katagiri
K. Koumoto
Publikationsdatum: 01.09.2008
Verlag: Springer US
Erschienen in: Journal of Materials Science / Ausgabe 17/2008
Print ISSN: 0022-2461
Elektronische ISSN: 1573-4803
DOI: https://doi.org/10.1007/s10853-008-2872-y

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht

Springer Professional

Abstract

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Springer Professional "Technik"

Weitere Artikel der Ausgabe 17/2008

Oxygen diffusion in Ti–10Mo alloys measured by mechanical spectroscopy

Preparation of gold/polyaniline/multiwall carbon nanotube nanocomposites and application in ammonia gas detection

Production of an austenitic steel matrix composite reinforced by in-situ nodular eutectic: the role of Si

Comparison of two contact models in the simulation of friction stir welding process

Fracture toughness analysis of anisotropic nickel-based single crystal superalloys at high temperature

Effect of finishing rolling temperature on fire resistance and dynamic strain aging behavior of a structural steel

Premium Partner

Marktübersichten