08.06.2021 | Composites & nanocomposites

Interface homogenization and its relationship with tensile properties of laser-arc hybrid welded Al/steel butt-joint via beam oscillation

verfasst von: Ming Gao, Yazhou Zhang, Yunfei Meng

Erschienen in: Journal of Materials Science | Ausgabe 25/2021

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

Homogenized intermetallic compound (IMC) layer at interface was achieved in laser-arc hybrid butt welded Al/steel dissimilar metals through beam oscillation. The beam oscillation reduced the macrosegregation of Fe element in the weld, which increased the uniformity of IMC layer by 443 times as its thickness variance (δ) decreased from 0.9767 to 0.0022. It was found that the tensile properties of weld were not only related to the thickness (τ) of IMC as claimed in most previous literatures, but also linked with its uniformity along interface. A new relationship between interface uniformity and tensile properties was established based on quantitative analysis of interface homogenization. The ultimate tensile strength was more than 130 MPa when δ ≤ 0.1156 and 0.9 μm ≤ τ ≤ 1.8 μm. Beam oscillation not only homogenized melt flow in molten pool, but also promoted to form turbulent flows at interface, which benefited for the interface homogenization.

Vorheriger Artikel An optional connection material in timber structures: densified poplar

Nächster Artikel A novel butterfly-shaped auxetic structure with negative Poisson’s ratio and enhanced stiffness

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Meco S, Pardal G, Ganguly S, Williams S, McPherson N (2015) Application of laser in seam welding of dissimilar steel to aluminium joints for thick structural components. Opt Lasers Eng 67:22–30CrossRef

Zhao S, Ni J, Wang G, Wang Y, Bi Q, Zhao Y, Liu X (2018) Effects of tool geometry on friction stir welding of AA6061 to TRIP steel. J Mater Process Technol 261:39–49CrossRef

Derazkola H, Khodabakhshi F (2019) Underwater submerged dissimilar friction-stir welding of AA5083 aluminum alloy and A441 AISI steel. Int J Adv Manuf Technol 102:4383–4395CrossRef

Yuan R, Deng S, Cui H, Chen Y, Lu F (2019) Interface characterization and mechanical properties of dual beam laser welding-brazing Al/steel dissimilar metals. J Manuf Process 40:37–45CrossRef

Kuryntsev S, Morushkin A, Gilmutdinov A (2017) Fiber laser welding of austenitic steel and commercially pure copper butt joint. Opt Lasers Eng 90:101–109CrossRef

Wang H, Kawahito Y, Nishimoto K (2019) A laser joining system for titanium and polyethylene terephthalate plastic controlled by multiple signal sources. IEEE Trans Ind Electron 66(2):1255–1263CrossRef

Meng Y, Li X, Gao M, Zeng X (2019) Microstructures and mechanical properties of laser-arc hybrid welded dissimilar pure copper to stainless steel. Opt Laser Technol 111:140–145CrossRef

Xia H, Tao W, Li L, Tan C, Zhang K, Ma N (2020) Effect of laser beam models on laser welding-brazing Al to steel. Opt Laser Technol 122:105845CrossRef

Tan C, Zang C, Xia H, Zhao X, Zhang K, Meng S, Chen B, Song X, Li L (2018) Influence of Al additions in Zn-based filler metals on laser welding-brazing of Al/steel. J Manuf Process 34:251–263CrossRef

10.

Sun J, Huang J, Yan Q, Li Z (2016) Fiber laser butt joining of aluminum to steel using welding-brazing method. Int J Adv Manuf Technol 85:2639–2650CrossRef

11.

Sun J, Yan Q, Li Z, Huang J (2016) Effect of bevel angle on microstructure and mechanical property of Al/steel butt joint using laser welding-brazing method. Mater Des 90:468–477CrossRef

12.

Xia H, Tan C, Li L, Ma N (2018) In situ SEM observations of fracture behavior of laser welded-brazed Al/Steel dissimilar joint. J Mater Eng Perform 27(3):1047–1057CrossRef

13.

Li L, Xia H, Tan C, Ma N (2018) Effect of groove shape on laser welding-brazing Al to steel. J Mater Process Technol 252:573–583CrossRef

14.

Zhang Y, Li F, Guo G, Wang G, Wei H (2016) Effects of different powders on themicro-gap laser welding-brazing of an aluminium-steel butt joint using a coaxial feeding method. Mater Des 109:10–18CrossRef

15.

Wang L, Gao M, Zeng X (2019) Experiment and prediction of weld morphology for laser oscillating welding of AA6061 aluminium alloy. Sci Technol Weld Join 24(4):334–341CrossRef

16.

Hagenlocher C, Sommer M, Fetzer F, Weber R, Graf T (2018) Optimization of the solidification conditions by means of beam oscillation during laser beam welding of aluminum. Mater Des 160:1178–1185CrossRef

17.

Meng Y, Lu Y, Li Z, Zhao S, Gao M (2021) Effects of beam oscillation on interface layer and mechanical properties of laser-arc hybrid lap welded Al/Mg dissimilar metals. Intermetallics 133:107175CrossRef

18.

Dimatteo V, Ascari A, Fortunato A (2019) Continuous laser welding with spatial beam oscillation of dissimilar thin sheet materials (Al–Cu and Cu–Al): process optimization and characterization. J Manuf Process 44:158–165CrossRef

19.

Li C, Fan D, Wang B (2015) Characteristics of TIG arc-assisted laser welding-brazing joint of aluminum to galvanized steel with preset filler powder. Rare Met 34(9):650–656CrossRef

20.

Rathod M, Kutsuna M (2006) Use of pulsed CO₂ laser in laser roll bonding of A5052 aluminium alloy and low carbon steel. Weld World 50(7–8):28–36CrossRef

21.

Dharmendra C, Rao K, Wilden J, Reich S (2011) Study on laser welding-brazing of zinc coated steel to aluminum alloy with a zinc based filler. Mater Sci Eng A 528(3):1497–1503CrossRef

22.

Meng Y, Gong M, Zhang S, Zhang Y, Gao M (2020) Effects of oscillating laser offset on microstructure and properties of dissimilar Al/steel butt-joint. Opt Lasers Eng 128:106037CrossRef

23.

Gao M, Chen C, Gu Y, Zeng X (2014) Microstructure and tensile behavior of laser arc hybrid welded dissimilar Al and Ti alloys. Materials 7:1590–1602CrossRef

24.

Lazic V, Barbini R, Colao F, Fantoni R, Palucci A (2001) Self-absorption model in quantitative laser induced breakdown spectroscopy measurements on soils and sediments. Spectrochim Acta B At Spectrosc 56(6):807–820CrossRef

25.

Yi R, Guo L, Li C, Yang X, Li J, Li X, Zeng X, Lu Y (2016) Investigation of the self-absorption effect using spatially resolved laser-induced breakdown spectroscopy. J Anal At Spectrom 31(4):961–967CrossRef

26.

Meng Y, Li G, Gao M, Zhang C, Zeng X (2019) Formation and suppression mechanism of lack of fusion in narrow gap laser-arc hybrid welding. Int J Adv Manuf Technol 100:2299–2309CrossRef

27.

Nakamura H, Kawahito Y, Nishimoto K, Katayama S (2015) Elucidation of melt flows and spatter formation mechanisms during high power laser welding of pure titanium. J Laser Appl 27(3):032012CrossRef

28.

Li G, Zhang C, Gao M, Zeng X (2014) Role of arc mode in laser-metal active gas arc hybrid welding of mild steel. Mater Des 61:239–250CrossRef

29.

Zhang C, Gao M, Wang D, Yin J, Zeng X (2017) Relationship between pool characteristic and weld porosity in laser arc hybrid welding of AA6082 aluminum alloy. J Mater Process Technol 240:217–222CrossRef

30.

Olsen F (2009) Hybrid laser-arc welding. Woodhead Publishing Limited, CambridgeCrossRef

31.

Meng Y, Kang K, Gao M, Zeng X (2019) Relationship between corrosion resistance and microstructure characteristic of single-pass laser-arc hybrid welded stainless clad steel plate. Metall Mater Trans A 50A:2817–2825CrossRef

32.

Wang L, Gao M, Hao Z (2020) A pathway to mitigate macrosegregation of laser-arc hybrid Al-Si welds through beam oscillation. Int J Heat Mass Tran 151:119467CrossRef

Titel: Interface homogenization and its relationship with tensile properties of laser-arc hybrid welded Al/steel butt-joint via beam oscillation
verfasst von: Ming Gao
Yazhou Zhang
Yunfei Meng
Publikationsdatum: 08.06.2021
Verlag: Springer US
Erschienen in: Journal of Materials Science / Ausgabe 25/2021
Print ISSN: 0022-2461
Elektronische ISSN: 1573-4803
DOI: https://doi.org/10.1007/s10853-021-06234-0

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht

Springer Professional

Abstract

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Springer Professional "Technik"

Weitere Artikel der Ausgabe 25/2021

Preparation of organic-modified magadiite–magnetic nanocomposite particles as an effective nanohybrid drug carrier material for cancer treatment and its properties of sustained release mechanism by Korsmeyer–Peppas kinetic model

Intermediate temperature proton electrolytes based on cesium dihydrogen phosphate and poly(vinylidene fluoride-co-hexafluoropropylene)

Protein encapsulation in functionalized sol–gel silica: influence of organosilanes and main silica precursors

Nanostructured covalent organic frameworks with elevated crystallization for (electro)photocatalysis and energy storage devices

Architected poly(lactic acid)/poly(ε-caprolactone)/halloysite nanotube composite scaffolds enabled by 3D printing for biomedical applications

High-strength reduced graphene oxide paper prepared by a simple and efficient method

Premium Partner

Marktübersichten