Cross-linkable and thermally stable aliphatic polycarbonates derived from CO₂, propylene oxide and maleic anhydride

Poly(propylene carbonate maleate) (PPCMA) was successfully synthesized from carbon dioxide with propylene oxide and maleic anhydride using supported zinc glutarate as catalyst. The PPCMA can be readily cross-linked using dicumyl peroxide (DCP) as a cross-linking agent. The gel content, thermal performance and mechanical properties of the cross-linked PPCMA were then investigated. The results showed that the gel content increased with increasing DCP content and reaction temperature. The as-prepared PPCMA showed higher glass transition temperature (T _g) and decomposition temperature compared with uncross-linkable poly(propylene carbonate) (PPC). The introduction of small amount of cross-linkable moiety provides a very effective way to improve the thermal stability and to extend the molecular weight of PPC, consequently extending its application area.