01.07.2012 | Original Paper

Sol–gel template synthesis and characterization of VO₂ nanotube arrays

verfasst von: Chunming Huang, Lihua Chen, Gang Xu, Lei Miao

Erschienen in: Journal of Sol-Gel Science and Technology | Ausgabe 1/2012

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

In this paper, we report on the obtention of highly ordered VO₂ nanotube arrays synthesized by the simple sol–gel template method. Techniques of transmission electron microscopy, X-ray powder diffraction, X-ray photoelectron spectroscopy, Raman spectroscopy were used to characterize the morphology and structure of the as-synthesized nanotube arrays. It is found that the size of the as-obtained nanotubes has the dimension of 180–220 nm in outer diameter, 110–140 nm in inner diameter and up to 10 μm in length. The results show that as-synthesized sample is assigned to VO₂ (B) phase in expected V/O ratio with V existing in the +4 oxidation state.

Vorheriger Artikel Preparation and optical properties of high-quality oriented of Al and Er co-doped ZnO thin films

Nächster Artikel Novel preparation method of nanosilver doped sol gel TiO2 photocatalysts for dye pollutant degradation

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Sun D, Kwon CW, Baure G, Richman E, Maclean J, Dunn B, Tolbert SH (2004) Adv Funct Mater 14:1197CrossRef

Guerra EM, Mulato M (2009) J Sol–Gel Sci Technol 52:315CrossRef

Guerra EM, Cestarolli DT, Oliveira HP (2010) J Sol–Gel Sci Technol 54:93CrossRef

Haras A, Witko M, Salahub DR, Hermann K, Tokarz R (2001) Surf Sci 491:77CrossRef

Wu X, Tao Y, Dong L, Wang Z, Hu Z (2005) Mater Res Bull 40:315CrossRef

Shi Q, Huang W, Yan J, Zhang Y, Mao M, Zhang Y, Xu Y, Zhang Y (2011) J Sol–Gel Sci Technol 59:591CrossRef

Liu J, Li Q, Wang T, Yu D, Li Y (2004) Angew Chem Int Ed 43:5048CrossRef

Tsang C, Manthiram A (1997) J Electrochem Soc 144:520CrossRef

Patzke GR, Krumeich F, Nesper R (2002) Angew Chem Int Ed 41:2446CrossRef

10.

Muhr HJ, Krumeich F, Schonholzer UP, Bieri F, Niederberger M, Gauckler LJ, Nesper R (2000) Adv Mater 12:231CrossRef

11.

Ahmad AL, Koohestani B, Bhatia S, Ooi BS (2010) J Sol–Gel Sci Technol 56:327CrossRef

12.

Baudrin E, Sudant G, Larcher D, Dunn B, Tarascon JM (2006) Chem Mater 18:4369CrossRef

13.

Zhang S, Li Y, Wu C, Zheng F, Xie Y (2009) J Phys Chem C 113:15058CrossRef

14.

Li G, Chao K, Peng H, Chen K, Zhang Z (2007) Inorg Chem 46:5787CrossRef

15.

Li X, Chen X, Chen X, Han C, Shi C (2007) J Cryst Growth 309:43CrossRef

16.

Armstrong G, Canales J, Armstrong AR, Bruce PG (2008) J Power Sources 178:723CrossRef

17.

Mao L, Liu C (2008) Mater Res Bull 43:1384CrossRef

18.

Sediri F, Gharbi N (2009) Mater Lett 63:15CrossRef

19.

Sediri F, Touati F, Gharbi N (2006) Mater Sci Eng B 129:251CrossRef

20.

Corr SA, Grossman M, Shi Y, Heier KR, Stucky GD, Seshadri R (2009) J Mater Chem 19:4362CrossRef

21.

Sediri F, Touati F, Gharbi N (2006) Mater Sci Eng B 129:251CrossRef

22.

Li J, Su Z, Yang B, Cai S, Dong Z, Ma J, Li R (2010) J Phys Chem Solids 71:407CrossRef

23.

Chen W, Peng J, Mai L, Yu H, Qi Y (2004) Solid State Commun 132:513CrossRef

24.

Chen X, Wang X, Wang Z, Wan J, Liu J, Qian Y (2004) Nanotechnology 15:1685CrossRef

25.

Jiao L, Yuan H, Wang YJ, Cao J, Wang YM (2005) Electrochem Commun 7:431CrossRef

26.

Silversmit G, Delpa D, Poelman H, Marin GB, Gryse RD (2004) J Electron Spectrosc Relat Phenom 135:167CrossRef

27.

Marques VS, Cavalcante LS, Sczancoski JC, Paris EC, Teixeira JMC, Varela JA, De Vicente FS, Joya MR, Pizani PS, Siu Li M, Santos MRMC, Longo E (2009) Spectrochim Acta A 74:1050CrossRef

28.

Wang XJ, Li HD, Fei YJ, Wang X, Xiong YY, Nie YX, Feng KA (2001) Appl Surf Sci 177:8CrossRef

29.

Schilbe P (2002) Physica B 316/317:600

30.

Mwakikunga BW, Sideras-Haddad E, Maaza M (2007) Opt Mater 29:481CrossRef

Titel: Sol–gel template synthesis and characterization of VO2 nanotube arrays
verfasst von: Chunming Huang
Lihua Chen
Gang Xu
Lei Miao
Publikationsdatum: 01.07.2012
Verlag: Springer US
Erschienen in: Journal of Sol-Gel Science and Technology / Ausgabe 1/2012
Print ISSN: 0928-0707
Elektronische ISSN: 1573-4846
DOI: https://doi.org/10.1007/s10971-012-2769-8

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht

Springer Professional

Abstract

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Technik"

Springer Professional "Wirtschaft+Technik"

Weitere Artikel der Ausgabe 1/2012

Tunable white light-emission of a CaW1−x Mo x O4:Tm3+, Tb3+, Eu3+ phosphor prepared by a Pechini sol–gel method

A novel synthesis and optical properties of cuprous oxide nano octahedrons via microwave hydrothermal route

Preparation of p-type CuCr1−x Mg x O2 bulk with improved thermoelectric properties by sol–gel method

Porous gadolinia-doped ceria with adjustable pore sizes using PI-b-PEO copolymer as the structure-directing agent

Combined effort of Fe-dextran and an RTIL towards formation of ionogel

Thermal and optical properties of novel polyurea/silica organic–inorganic hybrid materials

Premium Partner

Marktübersichten