Improvement of Quench Factor Analysis in Phase and Hardness Prediction of a Quenched Steel

The accurate prediction of alloys’ properties introduced by heat treatment has been considered by many researchers. The advantages of such predictions are reduction of test trails and materials’ consumption as well as time and energy saving. One of the most important methods to predict hardness in quenched steel parts is Quench Factor Analysis (QFA). Classical QFA is based on the Johnson–Mehl–Avrami-Kolmogorov (JMAK) equation. In this study, a modified form of the QFA based on the work by Rometsch et al. is compared with the classical QFA, and they are applied to prediction of hardness of steels. For this purpose, samples of CK60 steel were utilized as raw material. They were austenitized at 1103 K (830 °C). After quenching in different environments, they were cut and their hardness was determined. In addition, the hardness values of the samples were fitted using the classical and modified equations for the quench factor analysis and the results were compared. Results showed a significant improvement in fitted values of the hardness and proved the higher efficiency of the new method.