Crystallization Behavior of Perovskite in the Synthesized High-Titanium-Bearing Blast Furnace Slag Using Confocal Scanning Laser Microscope

The isothermal phase composition of high-titanium-bearing slag (23 mass pct TiO₂) under an argon atmosphere during cooling process from 1723 K (1450 °C) was calculated by FactSage.6.3 (CRCT-ThermFact Inc., Montréal, Canada). Three main phases, which were perovskite, titania spinel, and clinopyroxene, could form during the cooling process and they precipitated at 1713 K, 1603 K, and 1498 K (1440 °C, 1330 °C, and 1225 °C), respectively. The nonisothermal crystallization process of perovskite in synthesized high-titanium-bearing slag was studied in situ by a confocal scanning laser microscope (CSLM) with cooling rate of 30 K/min. The results showed that the primary phase was perovskite that precipitated at 1703 K (1430 °C). The whole precipitation and growth process of perovskite was obtained, whereas other phases formed as glass under the current experimental conditions. Perovskite grew along a specific growth track and finally appeared with snowflake morphology. The growing kinetics of perovskite formation from molten slag were also mentioned.