Specific Features of the Magnetic Anisotropy of Thin Yttrium Iron Garnet Films Prepared by Pulsed Laser Deposition
Erschienen in: Physics of Metals and Metallography | Ausgabe 11/2018
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
The specific features of dependences of the magnetic anisotropy constants on the thickness of yttrium iron garnet films prepared by pulsed laser deposition were studied. Films with thicknesses of 96–333 nm were produced by pulsed laser evaporation of the target material and deposition onto gadolinium-gallium-garnet substrates with the (111) orientation. The results of an investigation into static magnetic properties showed that the saturation magnetization decreases as the films get thinner. The high-frequency properties were studied by ferromagnetic resonance (FMR). The uniaxial and cubic anisotropy fields and the relaxation parameter were determined by analyzing the angular dependences of the resonance field and the FMR line width. It was found that as the thickness decreases, the strength of the uniaxial anisotropy field increases monotonically, while the cubic anisotropy field decreases and reverses its sign.