Low-temperature sintering and microwave dielectric properties of Li4Mg3Ti2O9 ceramics by a sol–gel method
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 12/2018
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
The pure phase Li4Mg3Ti2O9 with nanopowders of 37 nm was prepared by a sol–gel method and calcinated at 600, 450 °C lower than that by a conventional solid-stated method. The sintering temperature of Li4Mg3Ti2O9 with addition of LiF (≥ 2 wt%) was reduced from 1275 to 800 °C with enhancement of density and microwave dielectric properties, related to the substitution of F− ion for O2− ion in Li4Mg3Ti2O9 compound at low temperature. Addition of LiF broadened the sintering window (800–1000 °C). The Li4Mg3Ti2O9–4 wt% LiF ceramic sintered at 850 °C exhibited good microwave dielectric properties of εr = 17.5, Q × f = 89,320 GHz (at 9.1 GHz), and τf = − 37.4 ppm/°C. Such samples were compatible with Ag electrodes, promising to be a candidate material for low-temperature co-fired ceramics technology application.