Low-temperature sintering and microwave dielectric properties of TiO2-based LTCC materials
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 12/2010
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
Temperature stable high-K LTCC material was prepared. The influence of fabrication process on the crystalline phases, microstructures and microwave dielectric properties of TiO2-Bi2O3-CuO ceramics were investigated. The crystalline phases and microstructures of TiO2-Bi2O3-CuO ceramics were investigated by X-ray diffraction, scanning electron microscopy and energy dispersive X-ray spectroscopy. It was found that rutile TiO2 phase and Bi2Ti4O11 phase co-existed in the TiO2-Bi2O3-CuO ceramics. Separate TiO2 grains and Bi2Ti4O11 grains distributed uniformly in the ceramic matrix. The composition 0.92TiO2-0.08Bi2Ti4O11 with 2 wt% CuO addition that was sintered at 900 °C for 2 h showed high dielectric constant (εr ~ 81), high quality factor (Q × f ~ 3,500 GHz) and near zero temperature coefficient of resonant frequency (τf ~ −5.1 ppm/°C), meanwhile the compatibility test showed that it could co-fire with silver electrode. The processing-microstructure-property interrelationship was also studied.