Microstructural Characteristics of Accumulative Roll-Bonded Ni-Al-Based Metal-Intermetallic Laminate Composite

The present investigation is an attempt to develop metal-intermetallic laminate composites based on Ni-Al system. In this study, Ni sheets and Al foils have been used for the development of Ni-Al laminate using accumulative roll-bonding technique at 773 K. The laminate composites were then subjected to the controlled annealing to affect reactive diffusion at the Ni/Al interface leading to intermetallic compound formation. The accumulative roll-bonded laminates showed good bonding of layers. Annealing treatment at 773 K led to formation of reaction product and maintained the interface integrity. A qualitative compositional analysis at the interfaces reflected the formation of Al-Ni compounds, and a gradual compositional gradient also across the interface. This process seems to be of promise so far as the continuous production of large scale metal-intermetallic laminate composites is concerned.