Microwave dielectric properties of Na⁺ and M³⁺-doped Ba(Mg_0.5W_0.5)O₃ ceramics

In this study, phase evolution, microstructure, and microwave dielectric properties of (Ba_0.98Na_0.02)(Mg_0.48M³⁺_0.02W_0.5)O₃ (M³⁺ = Al, Ga, Sc, In, Yb, Y, Dy, Gd, and Sm) ceramics sintered at 1700 °C for 1 h were investigated. All the compounds exhibited an ordered cubic perovskite structure. Regardless of the ionic radius of the doped M³⁺ ions, BaWO₄ was detected as the secondary phase in all the compounds. The field emission scanning electron microscopy (FE-SEM) images revealed a dense microstructure in all the compounds, except in the Al-doped compound, which exhibited an insufficient grain growth. The large and irregularly shaped grains indicated that the liquid phase sintering occurred. Splitting of the A_1g(O) mode was observed in the Raman spectra of large M³⁺ ion-doped compounds. Splitting of the F_2g modes did not occur and the bands were sharp, indicating that the cubic symmetry was retained. As the ionic radius of the doped M³⁺ ions increased, the dielectric constant (ε_r) increased slightly. The compounds doped with M³⁺ = Sc, In, Yb, and Y exhibited a very high quality factor (Q × f₀) in the range of 250,000 ~ 280,000 GHz. In the case of the compounds doped with M³⁺ = Al, Ga, Sc, In, Yb, Y, and Dy, the value of the temperature coefficient of resonant frequency (τ_f) was in the range of −24 ~ −19 ppm/°C, while the Gd and Sm-doped compounds exhibited positive values of 2.8 and 31.2 ppm/°C, respectively. The dielectric constant, quality factor, and temperature coefficient of resonant frequency of the In-doped compound, i.e., (Ba_0.98Na_0.02)(Mg_0.48In_0.02W_0.5)O₃, were 18.7, 286,557 GHz, and − 24.4 ppm/°C, respectively.