Nano-domain structure of Li₄Mn₅O₁₂ spinel

XRD-pure Li₄Mn₅O₁₂ spinels are obtained below 600 °C from oxalate and acetate precursors. The morphology consists of nanometric particles (about 25 nm) with a narrow particle size distribution. HRTEM and electron paramagnetic resonance (EPR) spectroscopy of Mn⁴⁺ are employed for local structure analysis. The HRTEM images recorded on nano-domains in Li₄Mn₅O₁₂ reveal its complex structure. HRTEM shows one-dimensional structure images, which are compatible with the (111) plane of the cubic spinel structure and the (001) plane of monoclinic Li₂MnO₃. For Li₄Mn₅O₁₂ compositions annealed between 400 and 800 °C, EPR spectroscopy shows the appearance of two types of Mn⁴⁺ ions having different metal environments: (i) Mn⁴⁺ ions surrounded by Li⁺ and Mn⁴⁺ and (ii) Mn⁴⁺ ions in Mn⁴⁺-rich environment. The composition of the Li⁺, Mn⁴⁺-shell around Mn⁴⁺ mimics the local environment of Mn⁴⁺ in monoclinic Li₂MnO₃, while the Mn⁴⁺-rich environment is related with that of the spinel phase. The structure of XRD-pure Li₄Mn₅O₁₂ comprises nano-domains with a Li₂MnO₃-like and a Li_4/3−xMn_5/3+xO₄ composition rather than a single spinel phase with Li in tetrahedral and Li_1/3Mn_5/3 in octahedral spinel sites. The annealing of Li₄Mn₅O₁₂ at temperature higher than 600 °C leads to its decomposition into monoclinic Li₂MnO₃ and spinel Li_4/3−xMn_5/3+xO₄.