In predicating the probability distribution of chloride diffusion coefficient of recycled aggregate concrete (DRAC), the morphological characteristics of three phases, i.e., the old attached mortar, the natural aggregate and the new mortar, should all be taken into account. The present paper attempts to develop a probability density evolution method (PDEM) to achieve this. After verifying the derived PDEM results with experimental results, the effects of old attached mortar to the DRAC are examined in a quantitative manner. It is found that (1) the variation of the attached mortar content is much sensitive to DRAC; (2) given the probability distribution of the content and chloride diffusion coefficient of old mortar, the probability distribution of DRAC can be analysed based on the PDEM; and (3) the critical chloride diffusion coefficient at a certain assurance rate can be obtained by the PDEM. The analysis results of this investigation will be valuable to the durability design for RAC.
Abkürzungen
Ara
Area fraction of RCA
Aoa
Area fraction of original (natural) aggregate in RCA
Aom
Area fraction of old mortar in RCA
CDF
Cumulative probability function
DRAC
Chloride diffusion coefficient of RAC
Dom
Chloride diffusion coefficient of old attached mortar in RAC
Dnm
Chloride diffusion coefficient of new mortar in RAC
Doa
Chloride diffusion coefficient of original aggregate
ITZ
Interfacial transition zone
NAC
Natural aggregate concrete
NCA
Natural coarse aggregate
PDEM
Probability density evolution method
PDF
Probability density function
RAC
Recycled aggregate concrete
RA
Recycled aggregate
RCA
Recycled coarse aggregate
RRCA
RCA replacement ratio
Rrm
Attached rate of old mortar or attached rate of residual mortar in RCA
1 Introduction
With a global intensification of the scarcity of resources in the twenty first century, the recycling of waste concrete is an important means for the implementation of a sustainable infrastructure development strategy. Compared with natural coarse aggregates (NCA), recycled coarse aggregates (RCA) have substantial characteristics in terms of uncertainties that arise from their complex composition (Wardeh et al. 2015). It is well-known that the properties of recycled aggregate concrete (RAC) are different from those of natural aggregate concrete (NAC) (Yehia et al. 2015; Wardeh et al. 2015). Previous theoretical analyses carried out in the framework of structural reliability theory and lab experiments have shown that: (1) higher scatter of the compressive strength of RAC affects the margins of structural safety (Breccolotti and Materazzi 2010); (2) the compressive strength of RAC varies with the RCA replacement percentage and it follows a normal probability distribution (Li et al. 2006); and (3) the durability of RAC can be strongly affected by the porosity and the high water absorption of the RCA (Debieb et al. 2010; Kou and Poon 2006). It is necessary to well understand the properties of RCA in order to control the behaviour of RAC. Some hypothetical problems related to durability aspects have resulted in RCA being employed only as base filler for pavement construction (Muscalu et al. 2013; Vancura et al. 2009), thereby and unnecessarily limiting the scope of application of RCA. The durability of concrete is of great concern, especially in high-chloride environments such as coastal areas and where de-icing salt is used in cold regions, and so determining the chloride diffusion characteristics of concrete is required in order to control the durability of concrete structures (Morga and Marano 2015). Additionally, the effects of water to binder ratios and mineral admixtures on RAC chloride diffusion coefficient have already been discussed by Kou and Poon (Kou et al. 2007), this investigation will only focus on the physical and geometrical characteristics of RAC.
Similarly to NAC, chloride ions contained in the surrounding environment can penetrate RAC, and thereafter induce corrosion of the embedded reinforcing steel bars. It is most important to quantify the chloride diffusion coefficient of RAC in order to better predict the initiation of corrosion (Care 2003). For the same volume of RAC, the diffusion coefficient of RAC increases with the content of old mortar (Xiao et al. 2012; Ying et al. 2013a). The application of RCA may increase the chloride penetration rate of RAC (Kou and Poon 2006; Kou et al. 2007). The chloride diffusivities of RAC generally increase with an increase of the RCA replacement ratio (Rrca); while for the same Rrca, the chloride diffusivities and the distribution of the chloride concentration in the modelled RAC still differ due to the effect of different distributions and arrangements of RCA (Ying et al. 2013b).
Anzeige
Because the old attached mortar in RCA is the main difference between RCA and NCA, determining the diffusion coefficient of old attached mortar in RCA is needed to control the chloride diffusion coefficient of RAC. The old mortar in RCA is related to several indices of concrete durability. For example, the main properties of RAC that are affected unfavourably by the attached mortar content are its density, absorption and Los Angeles abrasion, as well as the correlations between them and the attached mortar content (Juan and Gutierrez 2009). RCA produced with only primary crushing have significantly higher water absorption when compared to that of NCA, due to the presence of significant amounts of attached mortar (Gokce et al. 2011). Many pioneering investigations have been undertaken to remove or reduce the residual mortar. For this purpose, Tam et al. (2007) attempted to reduce the mortar attached to RCA by three pre-soaking treatment approaches, namely ReMortar (HCl), ReMortar (H2SO4) and ReMortar (H3PO4), while Abbas et al. (2007) proposed an equivalent mortar volume method to determine the residual mortar content of RCA. Furthermore, the old mortar stochastic distribution as well as its amount in RCA can be quantified by image analysis (Abbas et al. 2009). Therefore, it follows that the chloride diffusion coefficient of RAC has a stochastic distribution because of the stochastic distribution of old mortar in RCA (Abbas et al. 2009), and a stochastic service-life model for chloride-induced corrosion in reinforced RAC have been developed and implemented well by Srubar (2015).
In this paper, the RAC is idealised as a three-phase material, containing new mortar, old mortar and natural aggregates. A three-phase composite chloride diffusion coefficient model of RAC is built to predict its chloride diffusion coefficient. The diffusion coefficient of the old mortar (Dom) and the adhesive rate of the old mortar (Rrm) in RCA are taken as random variables. The probability density evolution method (PDEM) for the chloride diffusion coefficient analysis of RAC is then derived according to the three-phase composition material model. The advantage of this method is that the analytical probability density function (PDF) of RAC can be obtained, provided the probability distribution of the chloride diffusion coefficient of the old mortar and the content of the old mortar are known.
2 Significance of the Research
For the durability design of RAC, determining its chloride diffusion coefficient is essential. Due to the complexity and scatter of RAC at a mesoscopic scale, the probability distribution of chloride diffusion coefficient of RAC is needed to well understand. A probability density evolution method (PDEM) is developed in order to provide the foundation for a reliability analysis and a probabilistic approach for durability design of RAC structures.
3 Probability Density Evolution Method for RAC
3.1 Chloride Diffusion Coefficient Model of RAC
In analyzing the distribution of aggregate particles in concrete, it is usually assumed that aggregates in concrete, such as gravel, are spherical (Zheng and Li 2002). Based on the theoretical equations of Ying et al. (2013a), for Fuller aggregate gradation, the bigger the aggregate, the smaller is the volume fraction of ITZ around it. When the minimum diameter of aggregate is larger than 5 mm, the volume fraction of ITZ will become very small, and the influence of ITZ on the chloride diffusion coefficient for RAC can be neglected. In fact, the diameter of recycled coarse aggregate is usually larger than 5 mm. Therefore, in this investigation, it is assumed to take the recycled coarse aggregate concrete as a three-phase composite material: the new mortar, the old mortar and the natural aggregate. For simplicity, a two dimensional model is usually selected to study the chloride diffusion coefficient of concrete (Zheng et al. 2012). In this study, in order to verify old mortar distribution obtained from image analysis (Abbas et al. 2009), a two dimensional model will be constructed, see Fig. 1.
×
Anzeige
The dimension ra in Fig. 1 denotes the radius of the natural aggregate, rb − ra is the thickness of the old mortar in RAC and rc − rb is the thickness of the new mortar. To make the composite model be equivalent to that of a real concrete, ra, rb and rc should satisfy the following relationships:
where Aoa, Aom and Arca are the area fractions of the natural original aggregate, old mortar and recycled coarse aggregate, respectively; and Rrm is the old mortar adhesive rate.
The gradation of aggregate particles can be obtained from sieve particular analysis. Based on the theory of stereology (Zheng 2000), the probability density function for the spherical aggregates can be expressed by
where D is the diameter of spherical aggregate particles, which varies within the minimum aggregate diameter Dmin and the maximum aggregate diameter Dmax; and n is a coefficient denoting the type of aggregate gradation. For the equal volume fraction (EVF) gradation, n = 3.0, and for the Fuller gradation, n = 2.5. The ITZ area fractions in normal concrete have been obtained based on aggregate gradation by Zheng and Zhou (2007). Similarly, the old mortar area fraction (Aom) in RAC can be derived as
where NA is the number of recycled aggregate particles per unit area of concrete; h is the thickness of old mortar; and t1 and t2 are the coefficients of h. According to Eqs. (2) and (3), it can get \( A_{oa} = A_{RCA} \cdot \left( {1 - R_{rm} } \right) \). According to Zheng and Zhou (2007), \( 2\left\langle {R_{rca}^{{}} } \right\rangle \) and \( \pi \left\langle {R_{rca}^{2} } \right\rangle \) represent average diameter and area of circular RCA in the concrete, and for EVF (n = 3) and Fuller gradation (n = 2.5), there are
As a result, if the aggregate gradation, Dmin, Dmax, Arca, and Rrm are given, the old mortar area fraction Aom can be determined from Eq. (5), and the area fraction of new mortar Anm, can be simply determined as follows
$$ A_{nm} = 1 - A_{rca} $$
(12)
In deriving the chloride diffusion coefficient of RAC, let Dj be the chloride diffusion coefficient of the original aggregate (j = oa), old mortar (j = om), new mortar (j = nm) and RAC (j = RAC), respectively. For steady-state diffusion questions, the chloride content in the homogeneous medium of the jth phase constituent should satisfy the equation (Zheng and Zhou 2008):
Since the aggregate is relatively impermeable when compared with the new mortar and old mortar, this study assumes that Doa = 0. Thus, the radial chloride flux at the om − oa interface (r = roa) vanishes, i.e.
$$ q_{oa} (r_{a} ,\theta ) = 0 $$
(15)
To determine the chloride diffusion coefficient of the concrete, the radial chloride flux qnm(r, θ) at the outer boundary of the composite circle (r = rc) is specified by
where \( \overline{q} \) is a constant. As a result, the governing Eq. (13) with the boundary conditions given by Eqs. (15) and (16) forms a complete and well-posed boundary value problem. From the boundary conditions in Eqs. (15) and (16), it is evident that the solution to Eq. (13) is
the above two equations can be obtained. In order to eliminate the influence of circumstantial diffusion, the chloride content at the outer boundary at r = rc is expressed by
The relationship between \( \overline{q} \) and \( \overline{c} \) can be obtained by eliminating Aom1, Aom2, Anm1, Anm2, ra, rb, rc, from Eqs. (1), (2) and (19) to (24) as
On the other hand, if the composite circle of RAC is considered as a monolithic homogeneous medium with a chloride diffusion coefficient DRAC, it can be easily shown that \( \overline{q} \) is related to \( \overline{c} \) (Eq. (23)) by
The aggregate area fraction Ara and the adhesive rate of residual mortar Rrm are usually the most important parameters influencing the properties of RAC when the aggregate gradation is known (Poon et al. 2004). By defining the terms
Many pioneering investigators have studied the random distribution of Rrm (Abbas et al. 2009) and the chloride diffusion coefficient of conventional concrete (Zhang et al. 2011). However, the probabilistic information for DRAC is difficult to capture and quantify, and this has continued to be a difficult task for researchers. The following method may be used to obtain the probability distribution of DRAC based on the probability density evolution method (PDEM).
In Eq. (31), suppose that Ara and Dnm are constants and that 0 < Rrm ≤ 1, 1 × 10−6 mm2/s < Dom ≤ 15 × 10−6 mm2/s, and suppose that Rrm and Dom are continuous independent random variables, which follow the general probability density functions (PDFs) \( f_{{R_{rm} }} \left( {R_{rm} } \right) \) and \( f_{{D_{om} }} \left( {D_{om} } \right) \) respectively. In accordance with elementary probability theory (Walpole et al. 2011), the joint PDF is
It can be easily proved that the mappings U = u(Rrm, Dom) and V = v(Rrm, Dom) define a one-to-one transformation between the points (Rrm, Dom) and (u, v), so Eqs. (32) and (33) may be uniquely solved for Dom and Rrm in terms of u and v, and are given by
$$ R_{rm} \left( {u,v} \right) = \frac{1}{4}\frac{{D_{nm} A_{ra} v + 8D_{nm}^{2} A_{ra} + D_{nm} v - u + uA_{ra} }}{{D_{nm}^{2} A_{ra} }} $$
(35)
$$ D_{om} \left( {u,v} \right) = - \frac{{D_{nm} \left( {D_{nm} A_{ra} v + uA_{ra} - D_{nm} v + u} \right)}}{{D_{nm} A_{ra} v + 8D_{nm}^{2} A_{ra} + D_{nm} v - u + uA_{ra} }} $$
(36)
According to Walpole et al. (2011), the combined probability distribution of U and V is
The approach proposed above, which is one- and two-dimensional instead of being multi-dimensional, can be formulated and solved to produce the probability density evolution (PDF) of the random variable DRAC, which is termed as the probability density evolution method (PDEM).
3.3 Calibration for Probability Distribution of Old Attached Mortar Content
The general method to evaluate the PDF of chloride diffusion coefficient of RAC due to variation of the old attached mortar in RCA was successfully derived in last section, therefore, the PDF of old attached mortar needs to be determined in advance. A number of researchers (Tam and Tam 2007; Abbas et al. 2009) have investigated the content of old adhesive mortar in RCA. Abbas et al. (2009) investigated the distribution of the residual mortar content of RCA by the method of image analysis, which served as a quality control tool for such aggregates and which provided an accurate measurement of the residual mortar content in recycled aggregates. The average frequency of the RCA particles corresponds to four types of residual mortar distribution: A [RCA-MO (4.75–9.5 mm fraction)]; B [RCA-VA (4.75–9.5 mm fraction)]; C [RCA-VA (9.5–12.7 mm fraction)] and D [RCA-VA (12.7–19 mm fraction)]. RCA-MO and RCA-VA mean the RCA from Montreal and Vancouver, respectively. The residual mortar content is the weight-based Rrmw, while the residual mortar content in the current paper is the area-based Rrm, with the relationship between them being
where Gom and Goa are the relative densities (specific gravities) of old mortar and original aggregates, respectively.
After converting the histogram of Rrmw into the histogram of Rrm by using Eq. (47), the probability density values of Rrm can be calculated (Walpole et al. 2011). The equations of Weibull and Chi squared distribution are shown in Eq. (48) and Eq. (49) Substitution of x with Rrm in the following two definitions is used to fit the probability density values of Rrm with the data A, B, C, D, respectively, producing the results displayed in Fig. 2. There is some scatter for Rrm distribution because that recycled coarse aggregates from two sources representing totally different geographical locations and geological environments (Abbas et al. 2009).
It can be seen from these figures that, except for the data with relative large Rrm, the data fits well with the PDF. The variation of the PDF with Rrm can be divided into three stages: (i) the PDF of Rrm decreases sharply with an increase of Rrm when Rrm is less than 0.2; (ii) the PDF of Rrm decreases slowly with an increase of Rrm when Rrm is between 0.2 and 0.95; and (iii) the PDF of Rrm increases with an increase of Rrm when Rrm is beyond about 0.95. The reason for this may be that the smaller the aggregate size, the more difficult the old mortar is removed during crushing process. In some experiments (Xiao et al. 2014), the recycled aggregate was sieved by using an iron sieve with the side size of 10 mm, then the recycled aggregate sieved was defined as continuous gradation according to aggregate gradation curves, which satisfy the standard for technical requirements and test method of sand and crushed stone (or gravel) for ordinary concrete. Therefore, if recycled aggregates are sieved to some extent, the variation tendency of the PDF with Rrm only has the first two stages, i.e., decreasing trend totally. As a result, the Weibull function and Chi Square function are suitable for describing the probability density distribution of Rrm.
3.4 Experimental Verification
Ordinary Portland cement with a 28-day compressive strength of 42.5 MPa was selected in this experimental study. The fine aggregate was river sand. Recycled coarse aggregate (RCA) was obtained from concrete waste with original strength grade of C30. According to JGJ 52-2006, the physical properties of the NCA and the RCA are listed in Table 1.
Table 1
The properties of the coarse aggregate.
Types
Size (mm)
Crushing index (%)
Bulk density (kg/m3)
Apparent density (kg/m3)
Water absorption (%)
Silt content (%)
RCA
25–31.5
24
1280
2500
6
0.5
NCA
25–31.5
5
1355
2700
0.5
0.2
Given the apparent density of mortar, original natural aggregate and recycled aggregate, the old mortar adhesive rate (Rrm) of RCA can be calculated by equations in Ref. (Ying et al. 2013a), after 100 tests, the probably density distribution and distribution function of old mortar adhesive rate of RCA is calculated by Statistics Toolbox in software MATLAB, see Fig. 3.
×
The mixture proportions for the NAC, RAC and mortar in this test are presented in Table 2. The volume fraction of coarse aggregate is 40 %, and the area fraction of coarse aggregate is 54 % for a section of concrete according to composited spherical model of RAC. The preparation and curing of the mix were conducted in the laboratory of Guangxi University in Nanning, PR China. Two-stage mixing approach was used to cast recycled concrete. The mixture was cast in more than thirty Φ103 mm × 300 mm PVC tubes and thirty 100 × 100 × 100 mm-cube moulds. All were compacted on a vibration table, the PVC end cap and plastic film were used to prevent evaporation, see Fig. 4, then demoulded a day after casting and water-cured in a standard curing room for 28 days. Each cylindrical concrete sample was cut to five pieces, and only three pieces located in the middle of the tube were used to chloride diffusion coefficient test by the rapid chloride test method (RCM), see Fig. 5, according to Standard for test methods of long-term performance and durability of ordinary concrete. Sixty chloride diffusion coefficients with series I, thirty for series II and three for series III were obtained by RCM test, and the probability density distribution of data with series I is calculated by the Statistics Toolbox in software MATLAB, see Fig. 6. The mean value of chloride diffusion coefficient of new mortar is 3 × 10–6 mm2/s by RCM test. It is assumed that the chloride diffusion coefficient of natural aggregate is zero (Ying et al. 2013a), then the chloride diffusion coefficient of old mortar (Dom) can be calculated as 10 × 10–6 mm2/s by comparing value in series I and series II according to composited spherical model (Ying et al. 2013a). Given the information above, the probability distribution of DRAC can be calculated by PDEM, as shown in Fig. 6.
Table 2
Mix proportion by mass.
Series
Portland cement
Water
Fine aggregate
RCA
NCA
Polycarboxylate superplasticizer (%)
I
1
0.4
1.44
2.17
0.3
II
1
0.4
1.44
2.34
0.3
III
1
0.4
1.44
×
×
×
It can be illustrated from Fig. 6 that, the probable density distribution of RAC by PDEM is similar to that by RCM test although there is some difference. The mean value by RCM test is a little larger than that by PDEM, the reason may be that the ITZ is not considered in this study, the influence ITZ of RCA on the DRAC can be ignored when the partial size is larger than 5 mm (Ying et al. 2013a). Therefore, the PDEM can be verified to calculate the probable distribution of chloride diffusion coefficient of RAC.
3.5 Parametric Analysis
To analyse the effect of attached old mortar on DRAC, the following three aspects should be addressed. The first aspect involves a sensitivity analysis of the effects of Dom and Rrm on DRAC; the second aspect analyses the verification of PDEM with Monte Carlo method; and the third part is an analysis of the effect of both Rrm and Dom on DRAC using the PDEM. It should be noted that, this study emphasizes on effects of the random of old attached mortar on the random of chloride diffusion coefficient of RAC, therefore, effects of recycled aggregate contents and particle size distribution on chloride diffusion coefficient have not been discussed in the following analysis.
3.5.1 Sensitivity Analysis
To investigate the effect of Dom on the chloride diffusion coefficient of concrete, according to the parameter assignment given by Zheng and Zhou (2008) and Xiao et al. (2012), it is assumed that Dnm = 2 (×10–6 mm2/s), Rrm = 0.3, and let Dom = 3, 6, 9 (×10–6 mm2/s). With these parameters, the chloride diffusion coefficient of concrete can be determined from Eq. (31). The results are shown in Fig. 7.
×
As expected in Fig. 7a, DRAC varies with an increase of Ara for Dom = 3, 6, 9 (×10–6 mm2/s). The chloride diffusion coefficient of the concrete increases with an increase of Dom for a given Ara. When Dom increases from 3 to 9 (×10–6 mm2/s), DRAC increases by 21, 47, and 80 % for Ara values of 0.2, 0.4, and 0.6, respectively. The reason for this increase is that the aggregate is impermeable as assumed in this study, and the old mortar is more permeable than the new mortar. This implies that the chloride diffusion coefficient of old mortar can affect the chloride diffusion coefficient of concrete.
Setting Dnm = 2 (×10–6 mm2/s), Dom = 6 (×10–6 mm2/s) and Rrm = 0, 0.3, 0.5, and 0.7 produces the results in Fig. 7b. It can be seen from Fig. 7b that DRAC decreases with an increase of Ara for Rrm = 0, 0.3, and increases with an increase of Ara for Rrm = 0.7. The value of DRAC increases with an increase of the Rrm for a given Ara. When Rrm increases from 0 to 0.5, DRAC increases by 50, 133, and 300 % for Ara values of 0.2, 0.4, and 0.6, respectively. Furthermore, the influence of Rrm on DRAC seems more obvious than that of Dom according to comparisons between Fig. 7a, b. The reason may be that the variation rang of Dom is generally smaller than that of Rrm. The improvement of Rrm can increase the old mortar content and decrease the original aggregate content simultaneously for a given Ara. The value of Rrm may be more sensitive to DRAC than that of Dom.
Therefore, in order to reduce the chloride diffusion coefficient of RAC, Dom and Rrm need to be decreased by reducing the water/binder ratio and using pre-soaking approaches (Tam and Tam 2007), carbonizing recycled aggregate (Kou et al. 2014), and triple mixing method (Kong et al. 2010).
3.5.2 Comparison of PDEM with Monte Carlo Method
Monte Carlo method is often used to simulate chloride diffusion in concrete and has been verified by some experiments (Tikalsky et al. 2005). In order to compare PDEM with Monte Carlo method, according to analysis in last section, it is supposed that old mortar content obey Weibull (Rrm|0.6542, 0.9189), and chloride diffusion coefficient of old mortar obey Normal (Dom|7,1). 1000 random numbers are used for the distribution, see Fig. 8. Let Dnm = 2 (×10–6 mm2/s), Dom = 6 (×10–6 mm2/s) and Ara = 9/64π; and Rrm follow the distributions in Fig. 8a. With these inputs, the PDF of DRAC can be calculated according to Eqs. (31)–(33), as displayed in Fig. 9a. Let Dnm = 2 (× 10–6 mm2/s), Ara = 9/64π; Rrm follow the distributions in Fig. 8a, and Dom follow the distributions in Fig. 8b. With these inputs, the PDF of DRAC can be calculated according to Eqs. (31)–(33), as displayed in Fig. 9b.
×
×
It can be seen from Fig. 9 that, the chloride diffusion coefficient of RAC calculated by PDEM is in accordance with that by Monte Carlo method.
3.5.3 PDEM for DRAC with Variable Rrm and Dom
In many cases, the source of recycled coarse aggregates is uncertain. For example, some RCA came from buildings while some came from concrete pavements. Even for the same building, the quality of the concrete was different in different parts. Different types of waste concrete were usually collected together to produce recycled coarse aggregates, and the quality of old mortar in recycled aggregates is of course variable. The chloride diffusion coefficient of old mortar in RCA is also highly variable for different aggregates. The chloride diffusion coefficient of old mortar in RCA may follow a certain probability distribution.
In this study, the influence of old mortar in RCA on the chloride diffusion coefficient of RAC is focused on. For this reason, a modelled RAC that contains only one coarse aggregate is selected. Some researchers have investigated the probability distribution of the chloride diffusion coefficient of natural aggregate concrete (Zhang et al. 2011). However, the probability distribution of the diffusion coefficient of old mortar in RAC appears not to have been reported in literature. Therefore, the probability distribution functions of the chloride diffusion coefficient of conventional concrete are assumed to be similar to those of old mortar in recycled aggregates. According to Zhang et al. (2011), Dom is assumed to follow Weibull and Normal distributions.
The cumulative probability functions (CDF) of Rrm and Dom should satisfy
$$ \int_{\hbox{min} \left( x \right)}^{\hbox{max} \left( x \right)} {f\left( x \right){\text{d}}x = 1} $$
(50)
and therefore, the updated PDFs of Rrm and Dom are given by
where Rrm and Dom are in the range of 0 < Rrm ≤ 1 and 1 (×10−6 mm2/s) < Dom ≤ 15 (×10–6 mm2/s).
To compare the effects of the PDF of Rrm and Dom on the PDF of DRAC, the distributions of Rrm and Dom are listed in Table 3, in which A-W denotes the combination of the PDFs of Rrm with data A corresponding to Fig. 2a and the PDF of Dom with a Weibull distribution. Other designations are defined similarly. The PDFs of Rrm and Dom according to Table 3 are shown in Fig. 10. Let Dnm = 2 (× 10–6 mm2/s) and Ara = 9/64π. With these inputs, the PDF of DRAC can be calculated according to Eqs. (31)–(40), as displayed in Fig. 11a.
It can be seen from Fig. 11a that the PDF of DRAC varies in the range from 0.77 to 3.5 due to the limitations of Rrm and Dom. The PDF with A-W, C-W and C-N decreases sharply with an increase of DRAC when 0.77 (×10–6 mm2/s) ≤ DRAC < 1.2 (×10–6 mm2/s), then it decreases steadily with increasing DRAC when DRAC > 1.2 (×10–6 mm2/s). While the PDF with A-N decreases steadily with an increase of DRAC. The reason for this fall may be that both probability distribution of Rrm and Dom affect the probability distribution of DRAC, the decrease tendency of DRAC is corresponding to the old mortar probability distribution in Fig. 10.
The cumulative probability density functions (CDF) of DRAC can be obtained from Fig. 11a by
and are presented in Fig. 11b. It can be seen from these figures that the CDF of DRAC increases with the increase of DRAC. The probability of DRAC with C-W is larger than the others for a given DRAC value. Specifically, the probabilities of DRAC with A-W, C-W, A-N and C-N are 0.86, 0.93, 0.65 and 0.85 for a given DRAC = 2.0 (×10–6 mm2/s), respectively.
The accurate evaluation of the chloride diffusion coefficient of concrete is critical for the durability design of concrete, which usually requires a 95 % assurance rate of the DRAC for reliability. Therefore, the critical value of DRAC can be defined from Fig. 11b. If a 95 % assurance rate is required, the cross points between the line with the 95 % boundary and the lines with A-N, C-N, A-W and C-W can define the critical value of DRAC. Specifically, the DRAC with a 95 % assurance rate for lines A-W, C-W, A-N, C-N are 2.47, 2.11, 3.13 and 2.78, respectively. Additionally, if another assurance rate of DRAC is needed, this can be performed in a similar way.
3.5.4 PDEM for Variation of Chloride Diffusion Coefficient
To investigate the influence of PDEM on the variation of chloride diffusion coefficient of RAC, for simplified analysis, let Rrm follow Normal(Rrm|0.5,0.1) distribution with coefficient of variation 0.2, and Dom follow Normal(Dom|7,1) distribution with coefficient of variation 0.143, it should be noted that, any kind of probability distribution can be transformed into normal distribution by method of mapping transformation. With these inputs, the PDF of DRAC can be calculated according to Eqs. (22)–(40), and the data calculated by PEDM is fitted by normal distribution, as displayed in Fig. 12.
×
It can be seen from the figure that, the PDF of DRAC calculated by PEDM agrees well with Normal distribution, while after probability density evolution, the coefficient of variation of DRAC with 0.136 is different from that of Rrm and Dom.
4 Conclusion
In this paper, a simplified three-phase composite model has been proposed for predicting the chloride diffusion coefficient of recycled aggregate concrete (RAC). It should be noted that the model will not be appropriate for recycled fine aggregate, whose diameter is less than 5 mm. This investigations revealed that:
The newly proposed probability density evolution method (PDEM) can be applied to the analysis of the chloride diffusion coefficient for RAC.
The variation of residual mortar content in RAC is much sensitive to the chloride diffusion coefficient of RAC.
Weibull function and Chi Square function are suitable for describing the variation of the probability density function (PDF) of chloride diffusion coefficient of RAC.
The probability distribution of DRAC can be obtained from the probability distribution of Rrm and the probability distribution of Dom, and the coefficient of variation of DRAC is different from that of Rrm and Dom.
Acknowledgments
The authors acknowledge the financial support from the National Natural Science Foundation of China (NSFC) (51178340, 51408138), China Postdoctoral Science Foundation, Guangxi Natural Science Foundation (2014GXNSFBA118251). The first author would also like to thank the School of Civil and Environmental Engineering of UNSW.
Open AccessThis article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.