Phase, microstructural characterization and dielectric properties of Ca-substituted Sr₅Nb₄TiO₁₇ ceramics

The effect of Ca substitution for Sr on the phase, microstructure and microwave dielectric properties of the Sr_5−x Ca _x Nb₄TiO₁₇ composition series was investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM), an LCR meter, and vector network analyzer. Below 1450 °C, Sr_5−x Ca _x Nb₄TiO₁₇ (x = 1, 2, 3, or 4) compositions formed single-phase Sr₄CaNb₄TiO₁₇, Sr₃Ca₂Nb₄TiO₁₇, Sr₂Ca₃Nb₄TiO₁₇, and SrCa₄Nb₄TiO₁₇ ceramics, respectively. At x = 0 and 5, Sr₅Nb₄TiO₁₇ and Ca₅Nb₄TiO₁₇ formed, but along with Sr₂Nb₂O₇ (at x = 0) and CaNbO₃ and CaNb₂O₆ (at x = 5) secondary phases. Above 1450 °C, all the compositions formed two-phase ceramics. At low frequencies, a phase transition was observed in the composition Sr₅Nb₄TiO₁₇. The substitution of Ca for Sr enabled processing of highly dense Sr₂Ca₃Nb₄TiO₁₇, with ε_r ~ 53.4, τ_f ~ −6.5 ppm/°C and Q _u  × f _o  ~ 1166 GHz. Further investigations are required to improve the quality factor of these ceramics for possible microwave applications.